牌号简介 About |
---|
说明:STN7006是专为共挤薄膜和层压而开发的低密度聚乙烯(LDPE)。该树脂在机械、光学和刚度性能方面具有很大的结合。此外,STN7006的凝胶含量较低,保证了生产出外观优良的薄膜。根据ASTM D-4976-04A标准规范,本产品为PE 114。不含添加剂。该等级的最低生物基含量为95%,根据ASTM D6866测定。用途:用于共挤食品包装的高清晰度薄膜,如:奶酪、肉类、香肠、火腿片等。用于桌布、窗帘和层压组织的浇铸薄膜。卫生和清洁用固体、液体或糕点产品的软瓶子。工艺:吹膜挤出 Braskem PE STN7006 STN7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a great combination among mechanical, optical and stiffness properties. Besides STN7006 has low gels content which ensure a production of excellent appearance films. This product is identified as PE 114 according to ASTM D-4976-04a standard specification. Additives free. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Applications: High clarity films for coextruded food packaging, such as: cheese, meat, sausages, sliced ham, etc. Cast films for table cloth, curtains and laminated tissues. Flexible bottles for solids, liquids or pasties products for hygiene and cleanness. Flexible containers for cosmetics and pharmaceutical applications (complies with USP 37). Process: Blown Film Extrusion Braskem PE STN7006 STN7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a great combination among mechanical, optical and stiffness properties. Besides STN7006 has low gels content which ensure a production of excellent appearance films. This product is identified as PE 114 according to ASTM D-4976-04a standard specification. Additives free. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Applications: High clarity films for coextruded food packaging, such as: cheese, meat, sausages, sliced ham, etc. Cast films for table cloth, curtains and laminated tissues. Flexible bottles for solids, liquids or pasties products for hygiene and cleanness. Flexible containers for cosmetics and pharmaceutical applications (complies with USP 37). Process: Blown Film Extrusion Braskem PE STN7006 STN7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a great combination among mechanical, optical and stiffness properties. Besides STN7006 has low gels content which ensure a production of excellent appearance films. This product is identified as PE 114 according to ASTM D-4976-04a standard specification. Additives free. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Applications: High clarity films for coextruded food packaging, such as: cheese, meat, sausages, sliced ham, etc. Cast films for table cloth, curtains and laminated tissues. Flexible bottles for solids, liquids or pasties products for hygiene and cleanness. Flexible containers for cosmetics and pharmaceutical applications (complies with USP 37). Process: Blown Film Extrusion |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.60 | g/10min | ASTM D1238 |
Biobased Content Biobased Content |
95 | % | ASTM D6866 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
|||
2% 正割,TD,50 µm,吹塑薄膜 2% secant, TD, 50 µ m, blow molded film |
170 | MPa | ASTM D882 |
2% 正割,MD,50 µm,吹塑薄膜 2% secant, MD, 50 µ m, blow molded film |
140 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
TD,50 µm,吹塑薄膜 TD, 50 µ m, blow molded film |
g | ASTM D1922 | |
MD,50 µm,吹塑薄膜 MD, 50 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D2457 | ||
45°,50.0 µm,吹塑薄膜 45 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
60°,50.0 µm,吹塑薄膜 60 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
利安德巴塞尔BDO不可抗力情况更新
2017-09-25 尊敬的客户, 接上一封于2017年8月29日发布的公告,受飓风“哈维”影响,我们已暂停或减缓了我们位于德州钱纳尔维尤的1,4丁二醇(BDO)和其衍生物的生产,并就1,4丁二醇(BDO)和其衍生物宣布了不可抗力。不可抗力的生效时间为2017年8月29日。 由于这一事件,利安德化学公司于2017年9月5日实施了1,4丁二醇(BDO)及衍生物的供货调配措施,前溯至2017年9月1日生效。调货量取决于过去6月(2017年2月-7月)中签订货单的量。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |