牌号简介 About |
---|
低密度湿固化聚乙烯化合物,用于低压建筑电线、控制电缆和电缆槽应用(UL型SIS、XHH、XHW、XHW-2、RHH、RHW和RHW-2 VW-1),Pexidan® V/T是一种低密度交联聚乙烯系统,可通过水分固化,由硅烷预接枝基化合物A-3001和阻燃催化剂母料CAT-0组成。10fr.以适当的比例(50/50)混合和挤压,这两种成分形成一种材料,该材料可通过暴露在热水中进行固化。Pexidan® V/T是符合RoHS的系统。 Low density moisture curable polyethylene compound for low voltage building wire, control cable and cable tray applications (UL styles SIS, XHH, XHHW, XHHW-2, RHH, RHW, and RHW-2 VW-1). Also CSA listed for RW-90 and CIC (-40C rated). Pexidan® V/T is a low density XLPE system curable by moisture and consists of a silane pre-grafted base compound A-3001 and a flame-retardant catalyst masterbatch CAT-010FR. Mixed and extruded in the proper proportions (50/50), the two components result in a material that is curable by exposure to hot water. PEXIDAN ® V/T is halogenated but is RoHS-compliant. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.30 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
交叉结合的程度 The degree of cross combination |
60 | % | ASTM D2765 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
UL 1581 | ||
屈服 yield |
11.0 | MPa | UL 1581 |
断裂 fracture |
12.8 | MPa | UL 1581 |
断裂 fracture 2 |
MPa | UL 1581 | |
断裂 fracture 3 |
MPa | UL 1581 | |
断裂 fracture 4 |
MPa | UL 1581 | |
拉伸应变 Tensile strain |
UL 1581 | ||
断裂 fracture |
% | UL 1581 | |
断裂 fracture 2 |
% | UL 1581 | |
断裂 fracture 3 |
% | UL 1581 | |
断裂 fracture 4 |
% | UL 1581 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
变形 deformation |
% | UL 1581 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相对电容率 Relative permittivity |
|||
90℃ 90℃ |
UL 1581 | ||
击穿电压 breakdown voltage |
UL 1581 | ||
-- -- |
V | UL 1581 | |
after glancing impact after glancing impact |
V | UL 1581 | |
绝缘电阻 insulation resistance |
UL 1581 | ||
23℃ 23℃ |
Mohms/1000 ft | UL 1581 | |
90℃ 90℃ |
Mohms/1000 ft | UL 1581 | |
after 12 weeks:90℃ after 12 weeks:90℃ |
Mohms/1000 ft | UL 1581 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
极限氧指数 Extreme oxygen index |
|||
4.0 mm 4.0 mm |
% | ASTM D2863 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Crushing Test Crushing Test |
g | UL 1581 | |
高温伸长率 High temperature elongation 5 |
|||
负荷下伸长率,150℃ Elongation under load, 150 ℃ 5 |
% | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 After 60 day oil @ 75°C |
3 After 30 day gasoline @ 23°C |
4 After thermal ageing (7days @121°C) |
5 15 minutes, 0.2 N/mm² load |
【新闻资讯】查看全部
重磅!巨正源PDH配套丙烷低温储存系统(二)顺利投用
2021-12-30 搜料网资讯: 12月23日6时,随着首艘低温丙烷船卸船完成,东莞巨正源科技有限公司120万吨/年丙烷脱氢制高性能聚丙烯项目一期工程-丙烷低温储存系统(二)T-1202储罐首次进料成功,标 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |