牌号简介 About |
---|
在自然色试样上测量数据。 Data was measured on natural colored test specimens. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.42 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
1.7 到 2.3 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.16 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
6.4mm 6.4mm |
64 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
171 | ℃ | ASTM D648 |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
杜邦荣获Kapton低雾度黑色薄膜、掩盖膜全球专利
2017-05-04 杜邦电子与通讯事业部(简称杜邦)于近日宣布其有关杜邦Kapton黑色聚醯亚胺薄膜以及杜邦Pyralux黑色软性电路板材料进一步扩展其全球专利资产,这两项产品在手机装置、电脑、以及汽车的相关应用上都十分受到欢迎。 「Kapton黑色聚醯亚胺薄膜与Pyralux黑色软性电路板材料带领着新技术与薄型化电子应用实现高可靠性能。」杜邦电子材料事业部全球总裁Avi Avula表示:「恰逢4月27日是世界智慧财产权日(World Intellectual Property Day),专利 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |