牌号简介 About |
---|
HS5502XP是一种高密度聚乙烯共聚物,具有较高的抗应力开裂性能(ESCR),在机械性能和加工性能之间保持良好的平衡。用途:用于清洁产品、食品和家用电器的瓶子;工业用途的杰瑞罐。工艺:吹塑。 HS5502XP is a High Density Polyethylene, copolymer, that offers a high stress cracking resistance (ESCR) maintaining a good balance between mechanical properties and processability. Applications: Bottles for cleaning products, food products and household appliances; Jerrycans for industrial propose. Process: Blow Molding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.955 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,2.16kg 190℃,2.16kg |
0.35 | g/10min | ASTM D1238 |
190℃,21.6kg 190℃,21.6kg |
30 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
ASTM D1693 | ||
50 ℃,2.00 mm,10%非离子表面活性剂,模压成型,F50 50 ℃, 2.00 mm, 10% non-ionic surfactant, molded, F50 |
50.0 | hr | ASTM D1693 |
50 ℃,2.00 mm,100%非离子表面活性剂,模压成型,F50 50 ℃, 2.00 mm, 100% non-ionic surfactant, molded, F50 |
120 | hr | ASTM D1693 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,模压成型 Fracture, molded |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
|||
1% 正割,模压成型 1% cut, molded |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
模压成型 Compression Molding |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,模压成型 0.45 MPa, unannealed, molded |
℃ | ASTM D648 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
前2月规模以上工企利润大增178.9%
2021-03-29 搜料网资讯: 日前,国家统计局发布消息称,1~2月份,全国规模以上工业企业实现利润总额11140.1亿元,同比增长1.79倍,比2019年1~2月份增长72.1%,两年平均增长31.2%。 记者注意到,同比 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |