| 牌号简介 About |
|---|
| KetaSpire® KT-820 SL30是一种聚醚醚酮（PEEK）化合物，设计用于在干燥和外部润滑应用中提供优良的机械性能、耐磨性和低摩擦系数的平衡。该树脂由碳纤维、石墨和聚四氟乙烯（PTFE）组成的三元抗摩擦/耐磨添加剂体系配制而成。KetaSpire Peek是按照最高的行业标准生产的，具有独特的性能组合，包括优异的耐磨性、一流的抗疲劳性、易熔加工性、高纯度和对有机物、酸和碱的优异耐化学性。这些特性使其非常适合用于运输、电子、化学加工和工业用途，包括油气勘探和生产。树脂在自然状态下呈黑色。 KetaSpire® KT-820 SL30 is a polyetheretherketone (PEEK) compound designed to provide a balance of excellent mechanical properties, wear resistance and low coefficient of friction in both dry and externally lubricated applications. The resin is formulated with a ternary anti-friction/anti-wear additive system comprised of carbon fiber, graphite, and polytetrafluoroethylene (PTFE). KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity, and excellent chemical resistance to organics, acids, and bases. These properties make it well-suited for applications in transportation, electronics, chemical processing, and industrial uses including oil and gas exploration and production. The resin is black in color in its natural state. |
产品描述 Product Description
用途：轴承;薄膜;棒材;片材;工业应用;型材;衬套;飞机应用;齿轮;管件;
颜色：黑色
加工条件：注射成型 Injection Molding
性能特点： 防火阻燃等级V-0; 耐磨; 尺寸稳定性好; 耐化学性; 耐疲劳性好; 耐高温; 阻燃; Good Dimensional Stability,Flame Characteristics,High Heat Resistance,Fatigue resistance,Good wear resistance,Solvent resistance,V-0
填料：PTFE
| 技术参数 Technical Data | |||
|---|---|---|---|
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
-- -- |
69 | J/m | ASTM D256 |
|
-- -- |
9.0 | kJ/m² | ISO 180 |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
-- -- |
530 | J/m | ASTM D4812 |
|
-- -- |
34 | kJ/m² | ISO 180 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
291 | ℃ | ASTM D648 |
|
1.8 MPa，退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
|
玻璃化转变温度 Glass transition temperature |
℃ | ASTM D3418 | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
ASTM E831 | ||
|
0 到 150℃ 0 to 150 ℃ |
cm/cm/℃ | ASTM E831 | |
|
-50 到 50℃ -50 to 50 ℃ |
cm/cm/℃ | ASTM E831 | |
|
比热 specific heat |
DSC | ||
|
50℃ 50℃ |
J/kg/℃ | DSC | |
|
200℃ 200℃ |
J/kg/℃ | DSC | |
|
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM E1530 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
UL 94 | ||
|
0.80 mm 0.80 mm |
UL 94 | ||
|
1.60 mm 1.60 mm |
UL 94 | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 D，1 秒 Shore D, 1 second |
ASTM D2240 | ||
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
|||
|
-- -- 4 |
MPa | ASTM D638 | |
|
-- -- |
MPa | ISO 527-2/1A/1 | |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ISO 527-2/1A/5 | |
|
-- -- |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture 4 |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2/1A/5 | |
|
弯曲模量 Bending modulus |
|||
|
-- -- |
MPa | ASTM D790 | |
|
-- -- |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
-- -- |
MPa | ASTM D790 | |
|
-- -- |
MPa | ISO 178 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
|
剪切强度 shear strength |
MPa | ASTM D732 | |
|
摩擦系数 friction coefficient |
ASTM D3702 | ||
|
-- -- 5 |
ASTM D3702 | ||
|
-- -- 6 |
ASTM D3702 | ||
|
-- -- 7 |
ASTM D3702 | ||
|
-- -- 8 |
ASTM D3702 | ||
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
g/cm³ | ASTM D792 | |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
400℃，2.16kg 400℃，2.16kg |
g/10min | ASTM D1238 | |
|
收缩率 Shrinkage rate 3 |
ASTM D955 | ||
|
MD：3.2 mm MD：3.2 mm |
% | ASTM D955 | |
|
TD：3.2 mm TD：3.2 mm |
% | ASTM D955 | |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
% | ASTM D570 | |
|
熔体表观粘度 Apparent viscosity of melt |
|||
|
400℃，1000 sec^-1 400℃，1000 sec^-1 |
Pa·s | ASTM D3835 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 5" x 0.5" x 0.125" bars |
| 3 0.20 in/min |
| 4 润滑条件：: 75 fpm ， 1000 psi ( 0.38 m/s ， 6895 kPa) |
| 5 润滑条件： 800 fpm ， 750 psi (4.06 m/s ， 5171 kPa) |
| 6 干燥条件： 800 fpm and 31.25 psi (4.06 m/s and 215 kPa |
| 7 干燥条件：干燥条件： 200 fpm ，125 psi (1.02 m/s ， 862 kPa. 不推荐 50 fpm ，500 psi (0.25 m/s ， 3447 kPa).） |
|
【新闻资讯】查看全部 
信越化学将投资12.9亿美元建聚氯乙烯工厂
2021-01-28 搜料网资讯： 1月27日，日本信越化学宣布将投资12.8元美元，在美国建设聚氯乙烯工厂。 信越化学的美国子公司Shintech将在美国南部路易斯安那州的基地建设新工厂。该基地目前正在建设 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付