牌号简介 About |
---|
SABIC PP化合物2632/8是一种填充矿物的改性聚丙烯。典型的材料特性包括非常高的流动性和冲击和刚度之间的良好平衡,以及低收缩和CLTE的附加优势。典型应用包括大型汽车外部零件,如保险杠。SABIC PP化合物2632/8是指定的汽车等级。 SABIC® PPcompound 2632/8 is a mineral filled modified polypropylene. Typical material properties include a very high flow and an excellent balance between impact and stiffness with the added advantage of a low shrinkage and CLTE. Typical applications include large automotive exterior parts such as bumper. SABIC® PPcompound 2632/8 is a designated automotive grade. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.00 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
18 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
24 hrs 24 hrs |
0.85 | % | 内部方法 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃,注塑成型 23 ℃, injection molding |
无断裂 | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-40℃,注塑成型 -40 ℃, injection molding |
45 | kJ/m² | ISO 179/1eU |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/4A | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180-4A | |
0℃,注塑成型 0 ℃, injection molding |
kJ/m² | ISO 180-4A | |
23℃,注塑成型 23 ℃, injection molding |
ISO 180/4A | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
ASTM D696 | ||
-30 到 30℃ -30 to 30 ℃ |
cm/cm/℃ | ASTM D696 | |
23 到 80℃ 23 to 80 ℃ |
cm/cm/℃ | ASTM D696 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,注塑成型 Shaw's D, injection molding |
ISO 868 | ||
拉伸强度 tensile strength |
ISO 527-2/5/50 | ||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding |
MPa | ISO 527-2/5/50 | |
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
MPa | ISO 527-2/5/50 | |
拉伸应变 Tensile strain |
|||
断裂,3.20 mm,注塑成型 Fracture, 3.20 mm, injection molded |
% | ISO 527-2/5/50 | |
弯曲模量 Bending modulus 2 |
|||
注塑成型 injection molding 2 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法 I (三点负荷) |