Bayflex 110-50系统生产的固体聚氨酯弹性体在室温下的弯曲模量约为50000 psi*。该系统可与研磨玻璃纤维或矿物增强材料一起使用或不使用。Bayflex 110-50系统适用于需要优良冲击性能的应用,如汽车筋膜、农业和建筑设备、专用车辆和娱乐设备。Bayflex 110-50系统是一个合成橡胶反应注射成型(RIM)系统,作为两种液体成分提供。A组分为二苯基甲烷二异氰酸酯(MDI)预聚物,B组分为聚醚多元醇体系。与任何产品一样,在给定应用中使用Bayflex 110-50系统必须由用户提前进行测试(包括现场测试等),以确定适用性。 The Bayflex 110-50 system produces a solid urethane elastomer which has a flexural modulus of approximately 50,000 psi* at room temperature. This system can be used with or without milled glass fiber or mineral reinforcements. The Bayflex 110-50 system is used in applications requiring excellent impact properties such as automotive fascias, agricultural and construction equipment, specialty vehicles and recreational equipment. The Bayflex 110-50 system is a formulated elastomeric reaction injection molding (RIM) system supplied as two liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. As with any product, use of the Bayflex 110-50 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ASTM D792, ASTM D1622 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.70 | % | 内部方法 |
吸水率 Water absorption rate |
|||
40hr,3.18 mm 40hr,3.18 mm |
2.6 | % | 内部方法 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,3.18 mm Fracture, 3.18 mm |
19.3 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂,3.18 mm Fracture, 3.18 mm |
200 | % | ASTM D412 |
撕裂强度 tear strength 1 |
|||
3.18 mm 3.18 mm 1 |
kN/m | ASTM D624 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Heat Sag Heat Sag 3 |
ASTM D3769 | ||
4 in Overhang:121℃,3.18 mm 4 in Overhang:121℃,3.18 mm |
mm | ||
6 in Overhang:121℃,3.18 mm 6 in Overhang:121℃,3.18 mm |
mm | ||
Water Immersion(Length Increase,3.18 mm) Water Immersion(Length Increase,3.18 mm) |
% | 内部方法 | |
memo_intro memo_intro |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,3.18 mm Shaw D, 3.18 mm |
ASTM D2240 | ||
弯曲模量 Bending modulus |
ASTM D790 | ||
-30℃,3.18 mm -30℃,3.18 mm |
MPa | ||
23℃,3.18 mm 23℃,3.18 mm |
MPa | ||
65℃,3.18 mm 65℃,3.18 mm |
MPa | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:3.2 mm MD:3.2 mm |
1/℃ | ASTM D696 | |
热固组件 Thermosetting components 2 |
|||
部件 A Component A |
|||
部件 B Component B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 105 Index |
4 1 hr |
【新闻资讯】查看全部
诺维信与国投生物签署战略合作框架协议
2021-08-14 搜料网资讯: 近日,诺维信(中国)投资有限公司和国投生物科技投资有限公司签署生物能源与碳捕获和储存领域(BECCS)战略合作框架协议。诺维信中国区农业及工业生物解决方案副 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |