牌号简介 About |
---|
Braskem PE SLH0820/30AF SLH0820/30AF是由Braskem生产的LLDPE己烯共聚物。它具有优异的加工性能和优良的机械性能。非常低的凝胶量。该等级的最低生物基含量为84%,根据ASTM D6866测定。Braskem PE SLH0820/30AF说明:SLH0820/30AF是Braskem生产的LLDPE己烯共聚物。它具有优异的加工性能和优良的机械性能。非常低的凝胶量。该等级的最低生物基含量为84%,根据ASTM D6866测定。添加剂:无滑加工助剂中抗阻塞高应用:层压重型袋与低密度聚乙烯和高密度聚乙烯阀控重型袋混合 Braskem PE SLH0820/30AF SLH0820/30AF is a LLDPE produced by Braskem. It offers outstanding processability combined with excellent mechanical properties. Very low gel amount. The minimum biobased content of this grade is 84%, determined according to ASTM D6866. Additive: Slip Absent Processing Aid Medium Antiblocking High Applications: Lamination Heavy duty bags Blends with LDPE and HDPE Valvulated heavy duty bags Process: Blown Film Extrusion Braskem PE SLH0820/30AF SLH0820/30AF is a LLDPE produced by Braskem. It offers outstanding processability combined with excellent mechanical properties. Very low gel amount. The minimum biobased content of this grade is 84%, determined according to ASTM D6866. Additive: Slip Absent Processing Aid Medium Antiblocking High Applications: Lamination Heavy duty bags Blends with LDPE and HDPE Valvulated heavy duty bags Process: Blown Film Extrusion Braskem PE SLH0820/30AF SLH0820/30AF is a LLDPE produced by Braskem. It offers outstanding processability combined with excellent mechanical properties. Very low gel amount. The minimum biobased content of this grade is 84%, determined according to ASTM D6866. Additive: Slip Absent Processing Aid Medium Antiblocking High Applications: Lamination Heavy duty bags Blends with LDPE and HDPE Valvulated heavy duty bags Process: Blown Film Extrusion |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
Biobased Content Biobased Content |
84 | % | ASTM D6866 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
40.0 | MPa | ASTM D882 |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
50.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
|||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
弯曲模量 Bending modulus |
|||
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
MPa | ASTM D790 | |
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
MPa | ASTM D790 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
TD,25 µm,吹塑薄膜 TD, 25 µ m, blow molded film |
g | ASTM D1922 | |
MD,25 µm,吹塑薄膜 MD, 25 µ m, blow molded film |
g | ASTM D1922 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
中科炼化乙烯日均产量创新高
2022-03-02 中科炼化持续优化装置生产,加强安全管理,开展对标提升竞赛,进一步加大乙烯产量攻关。2月累计生产乙烯6.8万吨,超出月度计划1.7%。当月乙烯平均日产量达2439吨,创下装置投产以 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |