牌号简介 About |
---|
非热封胶带基膜NPU膜已开发出来,用作制造胶带的基膜。 Non Heat-sealable Tape Base Films NPU films have been developed for use as a base for the manufacture of adhesive tapes. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态 With oneself - dynamic |
0.25 | ASTM D1894 | |
与自身 - 静态 With oneself - static |
0.70 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
31 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:31 µm 1% secant, MD: 31 µ m |
> 3000 | MPa | ASTM D882 |
1% 正割,TD:31 µm 1% secant, TD: 31 µ m |
> 1500 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,31 µm MD, yield, 31 µ m |
MPa | ASTM D882 | |
TD,屈服,31 µm TD, yield, 31 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,31 µm MD, fracture, 31 µ m |
% | ASTM D882 | |
TD,断裂,31 µm TD, fracture, 31 µ m |
% | ASTM D882 | |
透氧度(湿)(23℃,31 µm,0.0% RH) Oxygen permeability (wet) (23 ℃, 31 µ m, 0.0% RH) |
cm³/m²/24 hr | ASTM F1927 | |
用量 dosage |
|||
31.2 µm 31.2 µm |
m²/kg | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
天津波音复材公司获787大型货舱门订单
2016-11-22 从天津波音复合材料有限公司获悉,日前该公司获得“787机型大型货舱门”项目。 天津波音所拥有的先进航空复合材料部件制造工艺,展示了波音全球供应商在工程和制造工艺上不断追求革新的精神,使得大型货舱门在波音总 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |