与普通玻璃相比,PMMA具有优异的抗冲击性能,但在塑料中相对较低,因此需要在这方面加以改进。LGMMA使用丙烯酸橡胶提高了PMMA的抗冲击性能,并保持了其耐候性。PMMA的抗冲击等级适用于需要冲击强度的区域,如标志牌、照明、显示器和自动售货机。 PMMA is excellent in impact resistance compared to general glasses, but relatively lower among plastics so it is demanded to be improved in this respect. LG MMA has improved the impact resistance of PMMA using acrylic rubbers, and maintained the weatherability. Impact resistant grade of PMMA is applied to the area where impact strength is required such as signboards, lightings, displays, and vending machines. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.17 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,3.80kg 230℃,3.80kg |
0.90 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 to 0.80 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.40 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
59 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
|||
3000 µm 3000 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
3000 µm 3000 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
河南洛阳将新建百万吨乙烯等系列项目
2021-01-28 搜料网资讯: 近日,洛阳市工信局正式印发十四五《洛阳市6+3+X新型产业专业园区建设推进方案》,方案中包括谋划建设洛阳高端石化产业园,主要内容如下: 在2021年,加快昊华含氟电 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |