| 牌号简介 About |
|---|
| SABIC® PPcompound 7600是一种矿物填充改性聚丙烯。这种材料结合了良好的流动，具有良好的冲击和高刚度水平，低收缩和CLTE。典型应用包括汽车外部零件，如大型薄壁零间隙保险杠设计，也包括侧壁板和保险杠条。它可以用于喷漆和未喷漆的应用，并根据需要添加紫外线稳定。SABIC® PPcompound 7600是指定的汽车等级。 SABIC® PPcompound 7600 is a mineral filled modified polypropylene. This material combines good flow, with a good impact and a high stiffness level and a low shrinkage and CLTE. Typical applications include automotive exterior parts such as large thin wall zero gap bumper designs but also lateral siding and bumper strips. It can be used in painted and unpainted applications with UV stabilization added on demand. SABIC® PPcompound 7600 is a designated automotive grade. |
产品描述 Product Description
用途：汽车防撞杆;汽车领域的应用;汽车外部零件;
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 可表面喷涂; 热膨胀系数低; 冲击性能好; 收缩性低; 耐候抗UV; 易流动; Good Rigidity,Weather resistance is good,Low CLTE,High impact resistance,Good liquidity,Sprayable,Low contractility
紫外线：UV Stabilized
填料：矿物
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.03 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
18 | g/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
24 hrs 24 hrs |
0.60 | % | 内部方法 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
ISO 527-2/5/50 | ||
|
屈服，3.20 mm，注塑成型 Yield, 3.20 mm, injection molding |
18.0 | MPa | ISO 527-2/5/50 |
|
断裂，3.20 mm，注塑成型 Fracture, 3.20 mm, injection molded |
15.0 | MPa | ISO 527-2/5/50 |
|
拉伸应变 Tensile strain |
|||
|
断裂，3.20 mm，注塑成型 Fracture, 3.20 mm, injection molded |
% | ISO 527-2/5/50 | |
|
弯曲模量 Bending modulus 2 |
|||
|
注塑成型 injection molding 2 |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃，注塑成型 23 ℃, injection molding |
ISO 179/1eA | ||
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
-40℃，注塑成型 -40 ℃, injection molding |
ISO 179/1eU | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/4A | ||
|
-20℃，注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180-4A | |
|
0℃，注塑成型 0 ℃, injection molding |
ISO 180/4A | ||
|
23℃，注塑成型 23 ℃, injection molding |
ISO 180/4A | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
ASTM D696 | ||
|
-30 到 30℃ -30 to 30 ℃ |
cm/cm/℃ | ASTM D696 | |
|
23 到 80℃ 23 to 80 ℃ |
cm/cm/℃ | ASTM D696 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 方法 I (三点负荷) |
|
【新闻资讯】查看全部 
喜讯！上海赛科成功打通物流大动脉 带动下游企业复工复产
2022-05-30 上海赛科严抓疫情防控，以路运转铁路、路运转水路等多种方式，成功打通物流大动脉，有效带动下游企业复工复产。目前，566名员工驻厂值守，生产运行处于安全可控状态。 丙烯腈 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付