牌号简介 About |
---|
Alathon® M6080是一种窄分子量分布的均聚物,具有增强的流动特性和良好的刚度和抗冲击平衡。典型应用包括箱子、手提箱、板条箱和托盘以及敞口桶。 Alathon M6080 is a narrow molecular weight distribution homopolymer that exhibits enhanced flow characteristics and good balance of stiffness and impact resistance. Typical applications include cases, tote bins, crates and trays and open-head pails. |
产品描述 Product Description
用途:容器;薄壁部件;工具/零件箱;装货箱;
加工条件:注射成型 Injection Molding
性能特点: 机械强度好; 均聚物; 窄分子量分布; 食品接触; 冲击性能好; 易流动; Good Rigidity,High impact resistance,Good liquidity,Food contact compliance,Weight distribution,Homopolymer
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.960 | g/cm³ | ASTM D1505 |
表观密度 Apparent density |
0.59 to 0.63 | g/cm³ | ASTM D1895 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
7.9 | g/10min | ASTM D1238 |
螺旋流动长度 Spiral flow length 2 , 3 |
21.8 | cm | Internal Method |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
80 | ASTM D2240 | |
拉伸模量 Tensile modulus 4 |
ASTM D638 | ||
-- -- |
MPa | ASTM D638 | |
1% 正割 1% secant |
MPa | ASTM D638 | |
拉伸强度 tensile strength 6 |
|||
断裂 fracture 5 |
MPa | ASTM D638 | |
屈服 yield 6 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 5 |
|||
断裂 fracture 5 |
% | ASTM D638 | |
弯曲模量 Bending modulus 6 |
ASTM D790 | ||
-- -- |
MPa | ASTM D790 | |
1% 正割 1% secant |
MPa | ASTM D790 | |
2% 正割 2% secant |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-18℃ -18℃ |
ASTM D4812 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
结晶峰温度 Crystallization peak temperature 12 |
|||
DSC DSC 12 |
℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 熔体温度: 440°F, 注塑压力: 1.00E+3 psi |
3 0.625 in |
4 类型 1, 2.0 in/min |
5 类型 4, 2.0 in/min |
6 0.49 in/min |