Lexan Exl1413t树脂Lexan Exl1413t聚碳酸酯(PC)硅氧烷共聚物树脂是一种透明的注塑级树脂。该树脂具有良好的低温(30°C)延展性,同时具有中等流动特性和良好的加工性能,与标准PC相比,具有更短的IM循环时间的机会。LEXAN™ EXL1413T resin是一种通用产品,有透明和不透明的颜色,是广泛应用的理想选择。阳离子。 LEXAN EXL1413T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 °C) ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1413T resin is a general purpose product available in transparent and opaque colors and is an excellent candidate for a broad range of applications. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PC Polycarbonate
用途:通用;
颜色:不透明,清晰/透明
加工条件:注射成型 Injection Molding
性能特点: 成型周期快; 共聚物; 防火阻燃等级V-2; 流动性中等; 机械强度好-延展; 易加工; Excellent Processability,Ductility,Quick molding cycle,Moderate liquidity,Copolymer,V-2
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ASTM D792 |
密度 Density |
1.19 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
9.50 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.40 to 0.80 | % | 内部方法 |
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 7 |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength 7 |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 8 |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
ASTM D3763 | ||
-30℃,Total Energy -30℃,Total Energy |
J | ASTM D3763 | |
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 9 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 10 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~80℃ TD:23~80℃ |
1/℃ | ISO 11359-2 | |
TD:-40~95℃ TD:-40~95℃ |
1/℃ | ASTM E831 | |
MD:23~80℃ MD:23~80℃ |
1/℃ | ISO 11359-2 | |
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
2.50 mm 2.50 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.8 mm 0.8 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
2540 µm 2540 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 5 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
|||
屈服,50 mm跨度 Yield, 50 mm span 4 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
L 级 Level L |
ISO 2039-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 80*10*3 sp=62mm |
8 80*10*3 |
9 80*10*4 mm |
10 速率 A (50°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
伊朗原油解禁在即 伊拉克寻求与中石化合资加强竞争力
2015-12-23 据《华尔街日报》报道,伊拉克正与中石化商讨共同组建一家石油营销公司的事宜。伊拉克此举正值伊朗原油将要获得解禁、国际油价暴跌至11年新低之际。伊拉克希望在严峻的环境下,更好地为之后更加激烈的竞争做好准备。 《华尔街日报》援引知情人士报道,伊拉克正与中石化商讨共同组建一家石油营销公司的事宜。具体来说,伊拉克方面计划和中石化各出资50%,在新加坡设立这家合资公司,专注于向中国销售伊拉克的石油。伊拉克方面会负责供应原油,中石化会负责提供融资支持。双方在合作的过程中,可能部署有竞争性 |
伊朗原油解禁在即 伊拉克寻求与中石化合资加强竞争力 据《华尔街日报》报导,伊拉克正与中国石化商议一同建立一家石油营销策划公司的事项。伊拉克这一举动恰逢沙特原油即将得到公开、国际原油价格狂跌至十一最低之时。伊拉克期待在不容乐观的自然环境下,能够更好地为以后更为猛烈的市场竞争充分准备。 《华尔街日报》引证知情人人员报导,伊拉克正与中国石化商议一同建立一家石油营销策划公司的事项。从总体上,伊拉克层面方案和中国石化各注资50%,在马来西亚开设这个合资企业,致力于向中国市场销售伊拉克的石油。伊拉克层面会承担供货原油,中国石化会承担出示股权融资适用。彼此在协作的全过程中,很有可能布署有竞争的条文分配。 《华尔街日报》称,伊拉克石油科长Adel Abdul-Mahdi表明12月21日会去中国,但未就行程安排的计划方案得出大量关键点。别的责任人也未公布大量关键点。 伊拉克与中国石化考虑到创建合资企业,恰逢原油市场狂跌皮软之时。这说明伊拉克期待在不容乐观的自然环境下,能够更好地为以后更为猛烈的市场竞争充分准备。 过去一年半的時间里,因为原油市场不断供过于求,石油价格出現了狂跌。布伦特原油原油在周一亚洲地区時间盘里再次大跌,更新2004年至今最低,坐落于36美元部位。美国宣布公布消除长达40年的原油出入口限令、沙特石油最开始将于下月得到公开,都给了原油市场大量工作压力。 沙特石油得到公开以后,国际性原油市场每日将有五十万桶附加的原油提供。上周五,美国宣布公布消除长达40年的原油出入口限令。专业人士觉得这一举动短时间对国际性油市不容易造成显著危害,但全世界原油供货提升必定存有小幅度放低石油价格的很有可能。 来源于:雅式橡塑制品网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
原厂数据及认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 手机皮革套
- 2019-04-28 0
- Lexan Exl1413t树脂Lexan Exl1413t聚碳酸酯(PC)硅氧烷共聚物树脂是一种透明的注塑级树脂。该树脂具有良好的低温(30°C)延展性,同时具有中等流动特性和良好的加工性能
- 阅读全文
手机皮革套
1-Lexan Exl1413t树脂Lexan Exl1413t聚碳酸酯(PC)硅氧烷共聚物树脂是一种透明的注塑级树脂
2-熔体体积流动速率(300℃/1.2 kg ) 9.50 cm³/10min
3-拉伸模量 2220 MPa
4-简支梁缺口冲击强度(-30℃) 60 kJ/m²
5-热变形温度(1.8 MPa,未退火,64.0 mm 跨距) 119 ℃
2-熔体体积流动速率(300℃/1.2 kg ) 9.50 cm³/10min
3-拉伸模量 2220 MPa
4-简支梁缺口冲击强度(-30℃) 60 kJ/m²
5-热变形温度(1.8 MPa,未退火,64.0 mm 跨距) 119 ℃