牌号简介 About |
---|
Menzolit® BMC 1100是一种基于不饱和聚酯树脂的整体模塑料。该产品是玻璃纤维增强,含有矿物填料。如果发生火灾,产品不会熔化,也不会形成液滴,也不会产生过量的烟雾。这种材料是在加热的钢模中压缩成型的。建议使用镀铬工具。该产品不含卤素。Menzolit® BMC 1100是一种用于高强度应用的特殊BMC。将玻璃含量设置为能够提供足够的可塑性和高强度和刚度特性的水平。树脂和玻璃纤维的选择在高机械负荷下提供了良好的性能,即使它们是循环或冲击式的。达到了UL 94规定的阻燃等级HB。典型应用是汽车工业和化学工程的功能部件。这种材料特别适用于高负荷或快速移动的部件。 Menzolit® BMC 1100 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® BMC 1100 is a special BMC for high strength application. The glass content is set to a level that provides sufficient mouldability with high strength and stiffness properties. The selection of the resin and glass fibres provide good properties at high mechanical loads even if they are cyclic or impact like. The fire retardancy level HB according to the UL 94 is achieved. Typical applications are functional components for the automotive industry and chemical engineering. The material is especially suited for highly loaded or fast moving components. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.80 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
-- -- 2 |
0.0 | % | DIN 53464 |
-- -- |
0.30 | % | ISO 2577 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
< 0.30 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
模压成型 Compression Molding |
13000 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
模压成型 Compression Molding |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
连续使用温度 Continuous use temperature |
℃ | 内部方法 | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Glow Bar Glow Bar |
IEC 60707-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Post Molding Shrinkage |
【新闻资讯】查看全部
克服塑料熔体在模腔内不规则脉冲活动的办法
2018-03-16 熔体注入型腔后先在模具腔壁上形成一层薄的表壳,当这层表壳在充模过程中受到后续熔料的挤压时,就会导致熔体破裂。 一旦很薄的表壳被撕破或发生移动,塑件表面即产生搓痕或皱纹。例如,在熔体指数较小的低密度聚乙烯塑件上,其表面径常可以看到明暗交替的条形区域,其产生的部位一般离浇口有一定距离,并遍布整个表面,尤其是薄壁塑件最容易产生这类故障,这主要是由于熔料在充填小熔腔尚未结束前受到较大的压力,导致熔体破裂,形成表面缺陷。 通常,减慢熔料在充模过程中的冷却速度和表壳层的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |