牌号简介 About |
---|
低压地下设施入口电缆用低密度湿固化聚乙烯化合物(UL型使用和使用-2)。Pexidan® U/T是一种低密度交联聚乙烯(XLPE)体系,可通过水分固化,由硅烷预接枝碱化合物A-3001和催化剂母料CAT-008组成。当以适当的比例(95/5)混合和挤压时,这两种成分会使材料在70-90°C热水或甚至环境湿度下固化。为了防止预烧焦,嫁接化合物和催化剂母粒必须单独存放,并且仅在使用时混合。Pexidan® U/T符合RoHS。 Low density moisture curable polyethylene compound for low voltage underground service entrance cables (UL styles USE and USE-2). PEXIDAN ® U/T is a low density XLPE system curable by moisture and consists of a silane pre-grafted base compound A-3001 and a catalyst masterbatch CAT-008. When mixed and extruded in the proper proportions (95/5), the two components result in a material curable by exposure to 70-95°C hot water or even ambient moisture. In order to prevent pre-scorching the grafted compound and the catalyst masterbatch must be stored separately and mixed only when used. PEXIDAN ® U/T is RoHS-compliant. PEXIDAN ® U/T is also suitable for medium voltage XLPE jacket applications not requiring flame retardancy. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
交叉结合的程度 The degree of cross combination |
72 | % | ASTM D2765 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
UL 1581 | ||
屈服 yield |
12.4 | MPa | UL 1581 |
断裂 fracture |
15.2 | MPa | UL 1581 |
断裂 fracture 2 |
MPa | UL 1581 | |
断裂 fracture 3 |
MPa | UL 1581 | |
断裂 fracture 4 |
MPa | UL 1581 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | UL 1581 | |
断裂 fracture 2 |
% | UL 1581 | |
断裂 fracture 3 |
% | UL 1581 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
老化测试 Aging test 5 |
UL 1581 | ||
Elongation after exposure Elongation after exposure |
% | UL 1581 | |
Original elongation Original elongation |
% | UL 1581 | |
Original tensile strength Original tensile strength |
MPa | UL 1581 | |
曝光后拉伸强度 Tensile strength after exposure |
MPa | UL 1581 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
变形 deformation |
% | UL 1581 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电常数 Dielectric constant |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
100 MHz 100 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
100 MHz 100 MHz |
ASTM D150 | ||
击穿电压 breakdown voltage |
UL 1581 | ||
-- -- |
V | UL 1581 | |
after glancing impact after glancing impact |
V | UL 1581 | |
绝缘电阻 insulation resistance |
UL 1581 | ||
23℃ 23℃ |
Mohms/1000 ft | UL 1581 | |
90℃ 90℃ |
Mohms/1000 ft | UL 1581 | |
after 12 weeks:90℃ after 12 weeks:90℃ |
Mohms/1000 ft | UL 1581 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Crushing Test Crushing Test |
g | UL 1581 | |
高温伸长率 High temperature elongation 6 |
|||
负荷下伸长率,150℃ Elongation under load, 150 ℃ 6 |
% | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 After 60 day oil @ 75°C |
3 After 30 day gasoline @ 23°C |
4 After thermal ageing (7days @121°C) |
5 300 hr. exposure |
6 15 minutes, 0.2 N/mm² load |
【新闻资讯】查看全部
雪松控股与广西钦州正式签署122亿化工新材料项目
2020-10-19 搜料网资讯: 共享合作新机遇 共建发展新格局2020年湾企入桂推介会暨签约仪式在深圳举行。签约仪式上,雪松控股与广西钦州市人民政府正式签署《投资合作协议》。雪松控股将在钦 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |