牌号简介 About |
---|
应用Neopor用于制造银灰色泡沫,其隔热性能比传统EPS产品要好得多。用于生产符合:DIN4102-B1(阻燃剂)EN ISO 13501-1-E产品说明的具有防火特性的膨胀泡沫,所述膨胀聚苯乙烯(EPS)含有均匀分布的阻燃剂。发泡剂:戊烷。有关防火性能的更多信息,请参见标题为“聚苯乙烯泡沫的防火性能”的技术信息表。Neopor® F 5300 Plus:适用于壁厚超过8毫米的砌块和型材。热导率提高。 Application Neopor® is used to manufacture silver-gray colored foams that have considerably better thermal insulation capacity than conventional EPS products. For the production of expanded foams having fire characteristics in conformity with: DIN 4102-B1 (flame retardant) EN ISO 13501-1-E Product description Expandable polystyrene (EPS) containing uniformly distributed flame-retardant. Blowing agent: pentane. Additional information pertaining to the fire behavior can be found in the technical information sheet titled "Fire -protec tion behavior of foams made of Styropor®". Neopor® F 5300 Plus : For blocks and shapes with wall thicknesses over 8mm. Thermal conductivity improved. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表观密度 Apparent density |
|||
-- -- 4 |
0.02 | g/cm³ | |
-- -- |
0.02 到 0.03 | g/cm³ | |
颗粒大小分布 Particle size distribution |
|||
< 800.0 µm < 800.0 µm |
< 2.0 | % | |
0.800 到 1.50 mm 0.800 to 1.50 mm |
> 95 | % | |
> 1.50 mm > 1.50 mm |
< 3.0 | % | |
含水量 water content |
% | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Aging(intermediate) Aging(intermediate) |
day | ||
珠子直径 Bead diameter |
mm |
备注 |
---|
1 Pentane |
2 一般属性:这些不能被视为规格。 |
3 Obtainable in a single pre-foaming operation |
【新闻资讯】查看全部
PE、PPR管道挤出存在成绩及处理方法
2017-06-02 一 、塑料挤出的基本原理 塑料加工业是一项综合性很强的技术型产业。它涉及到高分子化学,高分子物理,界面理论,塑料机械,塑料加工模具,配方设计原理及工艺控制等方面。挤出理论主要研究塑料在挤出机内的运动情况与变化规律。挤出机中塑料在一定外力作用下,于不同温度范围内出现的高聚物的三种物理状态,与螺杆结构,塑料性能,加工条件之间的关系。从而进行合理工艺控制。以达到提高塑料制品产量与质量的目的。塑料高分子材料,在恒定的压力下受热时,于不同温度范围内,出现玻璃态,高弹态,粘流态三种物理 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |