牌号简介 About |
---|
HIPREN® EM 1712 T TDAE(Hipren EM 1723)含有23.5%的苯乙烯,结合在聚合物中。每100.0份(w/w)聚合物中添加37.5份(w/w)低芳香族TDAE油。以树脂和脂肪酸皂为乳化剂,采用低温乳液共聚工艺生产橡胶,并用酸进行混凝。橡胶含有在生产过程中添加的染色稳定剂。该产品不含亚硝基胺。 HIPREN® EM 1712 T TDAE (HIPREN EM 1723) contains 23.5% styrene bounded in polymer. It is extended with 37.5 parts (w/w) of low aromatic TDAE oil per 100.0 parts (w/w) of polymer. The rubber is produced by low temperature emulsion copolymerization process with the use of resin and fatty acids soaps as emulsifiers and is coagulated by acid. The rubber contains a staining stabiliser added during the production process. The product is without nitrosoamine. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
门尼粘度 Mooney viscosity |
|||
ML 1+4,100℃ ML 1+4,100℃ |
49 | MU | ISO 289 |
结合苯乙烯 Combined with styrene |
23.5 | % | ISO 2453 |
Organic Acid Organic Acid |
4.5 | wt% | ISO 7781 |
Soap Soap |
0.5 | wt% | ISO 7781 |
Stabilizer Stabilizer 2 |
0.4 | wt% | |
灰份含量 Ash Content |
% | ISO 247 | |
挥发物 Volatiles |
wt% | ISO 248 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ISO 868 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 37 | |
300% 应变 300% strain |
MPa | ISO 37 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 37 | |
回弹性 Resilience |
% | ISO 4662 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time 3 |
ISO 6502 | ||
50%:160℃ 50%:160℃ |
min | ISO 6502 | |
90%:160℃ 90%:160℃ |
min | ISO 6502 | |
ETA Extract ETA Extract |
wt% | ASTM D5774 | |
焦化时间 Coking time 3 |
|||
160℃ 160℃ 3 |
min | ISO 6502 | |
Torque Torque 3 |
ISO 6502 | ||
Maximum:160℃ Maximum:160℃ |
dNm | ISO 6502 | |
Minimum:160℃ Minimum:160℃ |
dNm | ISO 6502 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10.4.2.1 |
3 Standard Test Recipie: ISO 2322; Mixing Procedure: ISO 2393; Carbon Black: IRB 7; Curemeter Test: Reometar MDR 2000; Conditions: Arc 0.5° |
【新闻资讯】查看全部
8月份规上工业企业利润同比增长10.1%
2021-09-29 搜料网资讯: 国家统计局发布数据显示,8月份全国规模以上工业企业利润同比增长10.1%,比2019年同期增长31.1%,两年平均增长14.5%。从1月份至8月份累计看,规模以上工业企业利润同比增 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |