牌号简介 About |
---|
Amodel AS -1945 HS是一种45 %玻纤增强级聚邻苯二甲酰胺(PPA)树脂,专门为了改善产品在50/50乙二醇和水环境中的性能而开发。此材料在226°F(108 ℃), 甚至在275 °F(135 ℃)测试温度下暴露于抗冻结剂时,性能超过汽车行业对聚合物材料的要求。 可用于各种汽车零部件,如节温器壳体、加热器核心端盖、加热器软管接头和进水口、电源插座及阀门灯。 -黑色: AS-1945 HS BK 324 本色: AS-1945 HS NT Amodel® AS-1945 HS is a 45% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material exceeds the performance required by the automotive industry for polymeric materials exposed to antifreeze at 226°F (108°C), even when tested at 275°F (135°C). Potential applications include a variety of automotive components such as thermostat housings, heater core endcaps, heater hose connectors, and water inlets, outlets and valves. Black: AS-1945 HS BK 324 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.57 | g/cm³ | ISO 1183/A |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD 3 |
0.60 | % | ASTM D955 |
MD MD 3 |
0.20 | % | ASTM D955 |
TD TD |
0.60 | % | ISO 294-4 |
MD MD |
0.20 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ASTM D638 | ||
-- -- 4 |
MPa | ASTM D638 | |
-- -- |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ASTM D638 | ||
断裂 fracture |
MPa | ISO 527-2 | |
断裂 fracture 4 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
屈服 yield |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | ISO 179-1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-- -- 4 |
J/m | ASTM D256 | |
-- -- |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
1 CPN 5101 |
2 一般属性:这些不能被视为规格。 |
3 D2类型 |
4 在275 °F(135 °C)下,浸渍于50/50乙二醇/水混合物1000小时 |
【新闻资讯】查看全部
上海石化塑料产品克服物流困难 有序推进复工复产
2022-05-09 随着疫情得到初步控制,上海周边企业有序推进复工复产。上海石化克服疫情给塑料产品公路跨省运输带来的困难,通过增加港口和铁路发货数量,在符合疫情防控要求的地点设置临时 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |