牌号简介 About |
---|
HIVOREX BL6200采用泥浆工艺技术生产。这种树脂非常适合用于吹塑应用。HIVOREX BL6200旨在提供高速可加工性,良好的ESCR。 HIVOREX BL6200 is produced by slurry process technology. This resin is ideally suited for use in blow molding application. HIVOREX BL6200 is designed to offer high speed processability, good ESCR. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.958 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.35 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
F50 F50 |
400 | hr | ASTM D1693 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
120 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
< -80.0 | ℃ | ASTM D746 |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
清点:国际外20+家阻燃塑料科技
2017-11-06 “阻燃”这个概念很久之前就存在了,中国最早的防火理论为“防患于未然”,《申鉴・杂言》记载“防为上,救次之,戒为下”。而世界上最早的公共消防队,诞生于中国的宋朝。宋人称消防队叫做“潜火队”“火隅”,列入军队编制。 当然,我们今天不是来了解阻燃材料的历史的,而是看看国外内阻燃材料企业的情况以及2017广州橡塑展上阻燃展品。话不多说,直接进入主题! 1、杜邦 2017年5月,中国广州――杜邦高性能材料事业部(DPM)于2017年5月15日首次推出全 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |