牌号简介 About |
---|
特点:高乙烯控制无规共聚聚丙烯;高清洁度和批次间均匀性;非常好的光学性能和计量控制;无滑动和防堵塞添加剂;适用于特殊薄膜配方;未处理表面的初始热封温度(IST)低于115°C。推荐用途:BOPP、铸造和TWQ薄膜热封共挤层;常规薄膜性能改性剂;注塑通用应用。 Characteristics: High ethylene control reologhy Random copolymer polypropylene; high cleanness and lot to lot uniformity; very good optical properties and gauge control; without slip and antiblock additives; ideal for special films formulations; Initial Heat Seal Temperature (IST) below 115 °C on non-treated face. Recommended for: BOPP, Cast and TWQ Films heat seal co-extruded layer; conventional film properties modifier; injection molding general purpose applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate 2 |
|||
230℃,2.16kg 230℃,2.16kg 2 |
7.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
20.3 | MPa | ASTM D638 |
拉伸应变 Tensile strain 3 |
|||
屈服,3.20 mm,注塑成型 Yield, 3.20 mm, injection molding 3 |
15 | % | ASTM D638 |
弯曲模量 Bending modulus 4 |
|||
1% 正割,3.20 mm,注塑成型 1% cut, 3.20 mm, injection molded 4 |
600 | MPa | ASTM D790-A |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm,注塑成型 23 ℃, 3.2mm, injection molding |
80 | J/m | ASTM D256-A |
落锤冲击 Drop hammer impact 5 |
|||
23℃,3.2 mm,注塑成型 23 ℃, 3.2 mm, injection molding 5 |
J | ASTM D5420 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 程序 B |
3 类型 1, 2.0 in/min |
4 类型 1, 0.051 in/min |
5 Method A |
【新闻资讯】查看全部
白到发光!TPE让白色或淡色手机壳亮丽如新!
2018-07-17 炎炎夏日,清凉的着装和装饰成为人们出街的标配。就连手机壳,也是应景地出现了各种靓丽明快的颜色。这其中,雪盈洁白的手机壳便成为了众多消费者的夏日清爽首选。 美中不足的是,白色或浅色手机壳却很容易在与牛仔裤接触时被弄脏,这使得手机壳制造商和消费者头疼不已。目前,除液体硅胶以外,其他材料尚不能有效解决这个问题,但硅胶材料的手机壳却又存在工艺复杂、模具易溢料、交货时间长等问题。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |