牌号简介 About |
---|
Borstar® ME6052是一种黑色双峰聚乙烯护套化合物,基于中密度基树脂,采用Borealis专有的Borstar双峰工艺技术生产。Borstar技术允许制造超出传统制造工艺和密度范围的聚合物,使其能够优化加工性能,减少收缩,同时提供良好的物理韧性和环境应力抗裂性(ESCR)。Borstar® ME6052含有2.5%分散性良好的炭黑,以确保优异的耐候性。Borstar® ME6052提供了平衡性能,在通信和能源电缆的制造、安装和寿命性能方面具有优势。Borstar® ME6052在使用声音挤压实践和测试程序进行加工时满足以下适用要求:ASTM D 1248 II型,C类,4类,E8、E9、J4 BS 6234:H03C型,TS2 DIN 57818/VDE 0818 EN 50290-2-24 HD 620 S1,第1部分,表4B,DMP 2、9、10、12、14、15 IEC 60502,ST3 IEC 60502型,ST7 IEC 60708 IEC 6084型0,ST3型,IEC 60840,ST7型,ISO 1872-PE,KCHL,33 D-006 NF C32-060 Borstar ME6052 is a black bimodal polyethylene jacketing compound, which is produced with the Borealis proprietary Borstar bimodal process technology. Borstar technology allows the manufacturing of polymers outside the traditional MFR and density range making it possible to optimize processability, reduce shrinkage and yet provide excellent physical toughness and environmental stress crack resistance (ESCR). Borstar ME6052 contains 2.5% well-dispersed carbon black in order to ensure excellent weathering resistance. Applications Borstar ME6052 is designed for: Jacket for energy and communication cables Borstar ME6052 offers a balance of properties giving advantages in manufacturing, installation and lifetime performance of communication and energy cables. Specifications Borstar ME6052 meets the applicable requirements as below when processed using sound extrusion practice and testing procedure: ASTM D 1248 Type II, Class C, Category 4, Grade E8, E9, J4 ISO 1872-PE, KCHL, 33 D-006 The following cable material standards are met by Borstar ME6052: EN 50290-2-24 DMP 2, 5, 7, 8, 9, 10, 12, 14, 15 Cables manufactured with Borstar ME6052 using sound extrusion practice normally comply with the following cable product standards: IEC 60502, Part 2, Type ST7 IEC 60708 IEC 60840, Type ST7 HD 603 S1, DMP 5, 7, 8 DIN VDE 0818 HD 620 S2, Part 1, table 4B, DMP 2, 9, 10, 12, 14, 15 UL 1072 Oil resistance I & II Special Features Borstar ME6052 consists of specially selected components to offer: Superior processability Excellent environmental stress cracking resistance (ESCR) Good abrasion & scratch resistance Low water permeability Superior heat deformation Good petroleum-jelly resistance Outstanding UV resistance Low shrinkage Good surface hardness |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
ISO 1183 | ||
-- -- 2 |
0.936 | g/cm³ | ISO 1183 |
-- -- 3 |
0.948 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.70 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
3.0 | g/10min | ISO 1133 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) 4 |
|||
条件 B,50 ℃,10%非离子表面活性剂,F0 Condition B, 50 ℃, 10% non-ionic surfactant, F0 4 |
> 5000 | hr | IEC 60811-4-1/B |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,1 秒 Shore D, 1 second |
ISO 868 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity 5 |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热压测试 Hot pressing test 6 |
|||
115℃ 115℃ 6 |
% | IEC 60811-3-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Base Resin, ISO 1872-2 |
3 Compound, ISO 1872-2 |
4 No crack |
5 Compound |
6 at high temperature, 6 hrs |
【新闻资讯】查看全部
把工业4.0理念带进模具消费制造进程
2017-05-12 1、什么是工业4.0 关于工业4.0,有很多的用途和讲法,不外乎利用网络的办法,把所有的东西连接起来,连通整个制造的部分。 那么,工业4.0对模具厂的帮助是什么? 我曾经任职一家在模具和制造领域非常知名的企业,有16年的时间。刚开始,主要做设计,后来到2002年,我们接到一个很大的订单。那时候要求我们每套模具的交期是7天,精度达到了mm级,能够在全球范围内互换。在2002年,这个任务是一项很大的挑战,而且数量很大,一个月有着200台的模具数量 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |