牌号简介 About |
---|
Prime LDPE 049是专为高性能成型应用而设计的低密度聚乙烯。这种分数熔融指数材料适用于需要高熔融强度、良好抗冲击性、柔韧性和出色的ESCR特性的应用。应用:Prime LDPE 049非常适用于药品、干果和肉类等包装应用。它也被用于计算机工业中的衬垫应用以及鼓衬。加工:在低于高密度聚乙烯(HDPE)或高密度聚乙烯(HMWPE)的温度下对LDPE 049工艺进行底漆处理。成型温度为295-320°F,刀具温度为100-130°F,模具收缩率为0.015-.020 in/in(机器方向),0.009-.011 in/in(横向)。表面处理:底漆LDPE 049可用热刀模切、冲压、剪切和切割。焊接通常是通过声波焊接来实现的。请与Primex塑料公司代表联系,了解有关表面处理、制造或热成型工艺的更多信息。颜色、纹理和功能:Prime LDPE 049颜色可匹配以满足您的特定要求。Primex将Prime LDPE 049挤出片材或辊料中,尺寸为.030-.200,宽度不超过64“。 Prime LDPE 049 is a Low Density Polyethylene specifically designed for high performance molding applications. This fractional melt index material is suitable for applications requiring high melt strength, good impact resistance, flexibility and outstanding ESCR characteristics. Applications: Prime LDPE 049 is ideal for packaging applications such as pharmaceuticals, dried fruits and meats. It is also being used for dunnage applications in the computer industry as well as for drum liners. Processing: Prime LDPE 049 processes at lower temperatures than HDPE or HMWPE. The forming temperature is 295-320°F and the tool temperature is 100-130°F. The mold shrink is .015 - .020 in/in in the machine direction and .009 - .011 in/in in the transverse direction. Finishing: Prime LDPE 049 can be die cut, punched, sheared and cut with a hot knife. Bonding is typically achieved by sonic welding. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures and Capabilities: Prime LDPE 049 can be color matched to meet your specific requirements. Primex extrudes Prime LDPE 049 in sheet or roll stock and in gauges of .030 - .200 and up to 64" in width. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.917 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.25 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
1.5 到 2.0 | % | |
TD TD |
0.90 到 1.1 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
23.9 | ℃ | ASTM D746 |
比热 specific heat |
J/kg/℃ | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Tool Temperature Tool Temperature |
℃ | ||
成型温度 Forming temperature |
℃ | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
节后,PVC市场交投清淡
2019-02-12 节后归来,PVC市场交投清淡,受期货上涨影响,部分商家报价跟随走高,但多数业者尚未返市,贸易商报价不多,观望为主。下游尚未开工,市场询盘寥寥,成交量有限。 春节期间,各地成交明显下滑,市场处于休市状态。节前下游备货较为充足,受春节长假影响,目前下游暂未开工,但PVC生产企业装置仍保持较高负荷运行,社会库存也呈小幅增长趋势。2月初至今,PVC企业库存量呈上升阶段,据监测显示,华东、华南市场库存量较节前将有明显增加,预计华东、华南PVC库存总量较节前增加3%左右,PVC生产企业 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |