牌号简介 About |
---|
PPS-HGR60是玻璃纤维增强PPS复合材料,以PPS树脂为基体填充玻璃纤维。聚苯硫醚化合物具有机械性能好、刚性高、抗蠕变、耐高温、阻燃、耐化学性好、电绝缘性能优良、耐电弧、吸水率低、模具收缩率低、易加工、尺寸稳定性好、耐辐射等特点。e.PPS-HGR60由于其高性能,广泛应用于航天航空、化工、电子电器、机械、汽车、铁路等领域,可用于制造航空中耐高温、电气绝缘至关重要的元件;防腐阀和电气绝缘件;精密插头;零件。发动机、终端等。 PPS-hGR60 is glass reinforced PPS compound, which is filled with glass fiber based on the PPS resin. The characteristic of PPS compounds includes good mechanical properties, high rigidity, high creep resistance, high temperature resistance, flame resistance, chemical resistance, excellent electrical insulation properties, arc resistance, low water absorption, low mold shrinkage, easy processing, good dimensional stability, and radiation resistance. Owing to its high performance, PPS-hGR60 is widely used in space aviation, chemical, electronic appliances, mechanical, automobile, railway fields etc. It can be used to make elements where high temperature resistance, electrical insulation are all-important in aviation; anticorrosion valves and electrical insulating parts; precise plugs; parts of engines, terminal etc. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.80 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
MD MD |
0.01 | % | ISO 294-4 |
TD TD |
0.32 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.02 | % | ISO 62 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
270 | ℃ | ISO 75-2/Af |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
维卡软化温度 Vicat Softening Temp |
|||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻 Volumetric resistance |
Ω.cm | IEC 60093 | |
表面电阻 Surface resistance |
Ω.cm | IEC 60093 | |
绝缘强度 Insulation strength |
|||
|
KV/mm | IEC 60243-1 | |
介电常数 Dielectric constant |
|||
|
IEC 60250 | ||
耗散因数 Dissipation factor |
|||
|
IEC 60250 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
|
V-0 | UL 94 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
GB / T 3398.2 - -200 | ||
拉伸强度 tensile strength |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 HRL |
【新闻资讯】查看全部
巴斯夫EPS材料为零下20℃的新冠疫苗运输保温护航
2021-02-26 搜料网资讯: 随着新冠疫苗的接种范围不断扩大,疫苗的运输需求也与日俱增。不同的疫苗须在不同的温度范围下储存和运输,但往往不 得不混放在同一车辆或冷库中。DHL等全球领先的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |