牌号简介 About |
---|
WR® 300是一种碳纤维增强压缩成型PEEK,通常由泵制造商和用户选择,用于泵衬套和泵壳或叶轮耐磨环。在清洁状态下可达到最大使用寿命。润滑和/或潮湿环境。WR® 300允许泵用户通过运行更紧密的磨损环间隙来提高泵效率,同时在泵出现空穴或出现径向轴承故障时降低泵的潜在损坏。 WR® 300 is a carbon-fiber reinforced compression molded PEEK™ often selected by pump manufacturers and users for pump bushings and case or impeller wear rings. Maximum service life is achieved in clean. lubricated and/or moist environments. WR 300 allows the pump user to increase pump effiency by running tighter wear ring clearances while decreasing potential pump damage when pumps are cavitated or experience radial bearing failures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.43 | g/cm³ | ASTM D792 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
316 | ℃ | ASTM D648 |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~143℃ MD:23~143℃ |
2.8E-5 | 1/℃ | |
最高使用温度 Maximum operating temperature |
135 | ℃ | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
93 | ASTM D2240 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
帝斯曼携手福特汽车,荣膺2017 SPE汽车创新奖
2017-12-07 以科技为立足之本,在全球范围内活跃于健康、营养和材料领域的荷兰皇家帝斯曼集团日前欣然宣布,其改性PA46 Stanyl® HGR2树脂助力福特汽车公司荣膺2017年度SPE汽车创新奖。该材料由帝斯曼工程塑料业务部与位于欧洲及北美的福特先进材料与工艺团队和福特产品开发团队合作开发,并在福特车辆上使用验证。这种低摩擦、高耐磨材料在材料类评选中胜出,已应用于福特F-150和Mustang两款车型的链条张紧器臂,并将很快应用于全球各地的福特车型。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |