牌号简介 About |
---|
说明:EPOCAST 35-A树脂/硬化剂927环氧树脂层压系统是一种双组分无溶剂材料,设计用于在300°F(149°C)以下的温度下工作。中粘度液体层压系统很容易弄湿玻璃织物;其较长的工作寿命支持大型复合材料维修的延长制造时间。EPOCAST 35-A树脂/硬化剂927环氧树脂层压系统非常适合于层压复合材料结构的修复或制造以及其他需要良好高温性能的应用。环氧树脂/硬化剂927环氧层压系统符合BMS 8-214的要求。 DESCRIPTION : Epocast® 35-A resin/Hardener 927 epoxy laminating system is a two-component, solvent-free material designed to perform at temperatures up to 300°F (149°C). The medium-viscosity liquid laminating system readily wets glass fabrics; its long work life supports extended fabrication times for large composite repairs. Epocast® 35-A resin/Hardener 927 epoxy laminating system is well suited for repair or fabrication of laminated composite structures and other applications requiring good high-temperatures properties. Epocast® 35-A resin/Hardener 927 epoxy laminating system is qualified to BMS 8-214. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
ASTM D792 | ||
-- -- 1 |
1.00 | g/cm³ | |
-- -- |
1.13 | g/cm³ | |
-- -- 2 |
1.19 | g/cm³ | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热固组件 Thermosetting components |
|||
树脂 resin |
按重量计算的混合比: 100 | ||
硬化法 Hardening method |
按重量计算的混合比: 25 | ||
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
25℃ 25℃ 19 |
cP | ||
25℃ 25℃ 20 |
cP | ||
25℃ 25℃ |
cP | ||
脱模时间 stripping time |
|||
83℃ 83℃ |
min | ||
后固化时间 Post curing time |
|||
121℃ 121℃ |
hr | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
工作期限 Working period |
|||
100 gms,25℃ 100 gms,25℃ |
ASTM D1338 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
弯曲模量 Bending modulus |
ASTM D790 | ||
25℃ 25℃ 3 |
MPa | ||
25℃ 25℃ 4 |
MPa | ||
25℃ 25℃ 5 |
MPa | ||
25℃ 25℃ 6 |
MPa | ||
弯曲强度 bending strength |
ASTM D790 | ||
25℃ 25℃ 7 |
MPa | ||
25℃ 25℃ 8 |
MPa | ||
25℃ 25℃ 9 |
MPa | ||
25℃ 25℃ 10 |
MPa | ||
压缩模量 Compression modulus |
ASTM D695 | ||
-- -- 11 |
MPa | ||
-- -- 12 |
MPa | ||
-- -- 13 |
MPa | ||
-- -- 14 |
MPa | ||
压缩强度 compressive strength |
ASTM D695 | ||
149℃ 149℃ 15 |
MPa | ||
149℃ 149℃ 16 |
MPa | ||
25℃ 25℃ 17 |
MPa | ||
25℃ 25℃ 18 |
MPa |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Hardener |
3 Resin |
4 Cure #1, After two hours boiling water |
5 Cure #2, After two hours boiling water |
6 Cure #1 |
7 Cure #2 |
8 Cure #1, 149°C |
9 Cure #2, 149°C |
10 Cure #1, 25°C |
11 Cure #2, 25°C |
12 Cure #1, tested at 149°C |
13 Cure #2, tested at 149°C |
【新闻资讯】查看全部
雀巢和乐购加入“全球幽灵装备计划”
2018-11-01 全球知名食品公司雀巢和英国知名连锁超市乐购已加入“全球幽灵装备计划”(GGGI),以帮助处理每年滞留在海洋中的超过64万吨的废弃渔具。 GGGI成立于2015年,是一个非盈利性质的全球联盟和机构,致力于在 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |