牌号简介 About |
---|
Aristech压克力有限公司SOLARCAST压克力板是一种“紫外线透射”铸造压克力板,源自独特的配方。Aristech Acrylics LLC Solarcast丙烯酸板是专为制革床和其他需要紫外线透射率的应用而开发的。使用0.177”(4.5 mm)厚的透明Aristech压克力有限责任公司压克力板测定以下物理性能。性能可能因其他厚度有所不同。 Aristech Acrylics LLC Solarcast® Acrylic Sheet is an "ultraviolet transmitting" cast acrylic sheet derived from a unique formulation. Aristech Acrylics LLC Solarcast® Acrylic Sheet was developed particularly for tanning bed and other applications where UV transmittance is needed. The following physical properties were determined using 0.177" (4.5 mm) thickness clear Aristech Acrylics LLC Acrylic Sheet. Properties may vary somewhat on other thicknesses. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.18 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
饱和,4.50 mm Saturation, 4.50 mm |
0.18 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
4.50 mm 4.50 mm |
315 | J/m | ASTM D6110 |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
4.5mm 4.5mm |
22 | J/m | ASTM D256-A |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,4.50 mm 1.8 MPa, unannealed, 4.50 mm |
95.6 | ℃ | ASTM D648 |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:4.5 mm MD:4.5 mm |
1/℃ | ASTM D696 | |
比热 specific heat 2 |
J/kg/℃ | ASTM C351 | |
导热系数 Thermal conductivity coefficient 2 |
W/m/K | 内部方法 | |
热稳定性 thermal stability 3 |
|||
180℃,4.50 mm 180℃,4.50 mm 3 |
ASTM D4802 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index 2 |
ASTM D542 | ||
透光率 Transmittance |
|||
4500 µm 4500 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
4500 µm 4500 µm |
% | ASTM D1003 | |
黄度指数 Yellowness index |
|||
4.50 mm 4.50 mm |
YI | ASTM D1925 | |
UV透过率 UV transmittance 4 |
|||
280 nm 280 nm |
% | ||
300 nm 300 nm |
% | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热成型温度 Hot forming temperature |
|||
4.50 mm 4.50 mm |
℃ | 内部方法 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级,4.50 mm M-grade, 4.50 mm |
ASTM D785 | ||
巴氏硬度 Babbitt hardness |
|||
4.50 mm 4.50 mm |
ASTM D2583 | ||
拉伸模量 Tensile modulus |
|||
4.50 mm 4.50 mm |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服,4.32 mm Yield, 4.32 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,4.50 mm Fracture, 4.50 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
4.50 mm 4.50 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
4.50 mm 4.50 mm |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.177 in |
3 30 min |
4 UV Spectrophotometer |
【新闻资讯】查看全部
卓宝荣获“高新技术企业”认定
2022-05-14 近期,湖北省科学技术厅公布了湖北省2021年高新技术企业认定结果的名单, 卓宝科技 旗下全资子公司湖北卓宝建筑节能科技有限公司(以下简称武汉卓宝生产基地)被认定为湖北省高 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |