牌号简介 About |
---|
Algoflon® L203一种由分散聚合产生的白色聚四氟乙烯微粉化粉末,由亚微米大小的主要颗粒的松散团块组成。Algoflon® L203可通过施加剪切力将其解聚至亚微米粒径,从而在应用中提供更好的聚四氟乙烯颗粒分散和分布。设计用于关键工程和高端性能润滑油,以提高稠化效果,润滑性,Algoflon® L203还提高了耐腐蚀性和耐温性。Algoflon® L203的主要特点是:高比表面积,低分子量,剪切下可分解性好。 Algoflon® L203 a white PTFE micronized powder produced from dispersion polymerization comprising loose agglomerates of sub-micon sized primary particles. Algoflon® L203 can be de-agglomerated to sub-micron particle size by the application of shear providing a better dispersion and distribution of the PTFE particles in the application. Designed for use in critical engineering and high end performance lubricants to improve thickening effect, lubricity, Algoflon® L203 improves also corrosion and temperature resistance. Main features of Algoflon® L203 include: High specific surface area Low molecular weight Good blendability Deagglomerated under shear |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
比表面积 Specific surface area |
> 7.5 | m²/g | 内部方法 |
平均颗粒尺寸 Average particle size |
|||
表面 surface |
5.0 | µm | 内部方法 |
体积密度 bulk density |
325 | g/l | ASTM D3418 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融峰值温度 Melting peak temperature |
325 到 335 | ℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
怎样选用塑料薄膜印刷用油墨
2017-10-19 塑料薄膜的印刷与纸张的印刷有所不同,除去前面所提到的预处理之外,另外一个问题就是薄膜表面光滑,不能让油墨渗透进去。纸张虽然表面看起来光滑,但实际上其表面是不光滑的,可以让油墨渗入,这样有利于油墨的迅速干燥成膜,也有利于油墨与纸张表面的粘结。 我们在选择油墨时,要考虑如下几个因素。 (1)热畸变点和耐热性 如果选择烘干型油墨时。就要考虑油墨的最大烘干温度与塑料所能承受的温度是否相宜。 (2)耐溶剂性 对塑料薄膜有一定溶解性的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |