部分水解级Mowiol和Kuraray Poval是Kuraray销售的聚乙烯醇的商品名。这些是由聚醋酸乙烯酯通过醇解使用连续工艺制造。通过改变聚醋酸乙烯的聚合程度及其水解程度(皂化),可以提供许多不同的等级。我们的pvoh类型以高标准纯度提供,特别是“低灰份和VOC含量”。 Partially hydrolysed grade Mowiol® and Kuraray Poval® are the trade name of the polyvinyl alcohols marketed by Kuraray. These are manufactured from polyvinyl acetate by alcoholysis using a continuous process. By varying the degree of polymerization of the polyvinyl acetate and its degree of hydrolysis (saponification), a number of different grades can be supplied. Our PVOH types are offered in a high standard purity showing especially "low ash and VOC contents". |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表观密度 Apparent density |
0.40 到 0.60 | g/cm³ | DIN 53466 |
溶液粘度 Solution viscosity 2 |
13 到 17 | mPa·s | DIN 53015 |
pH值 PH value 3 |
4.5 到 7.0 | DIN 19261 | |
灰份含量 Ash Content 4 |
< 0.50 | % | |
酯含量 Ester content |
180 到 220 | mg KOH/g | DIN 53401 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Degree of Hydrolysis Degree of Hydrolysis 5 |
% | ||
Residual Acetyl Content Residual Acetyl Content |
% | ||
不挥发物含量 nonvolatile content 6 |
% | DIN 53189 | |
甲醇可萃取 Methanol extractable |
% |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 4 % aqueous solution at 20 °C |
3 4 % solution in distilled water |
4 Calculated as Na2O |
5 Saponification |
6 After 3 hours' drying at 105 °C |
【新闻资讯】查看全部
改性塑料常见质量成绩及处理措施
2017-01-13 一、改性工艺流程 改性塑料的主要生产设备是双螺杆挤出机, 常见的生产工艺流程为:配料一混料一挤出一k拉条一冷却一切粒一包装。 改性塑料产品质量问题主要可分为外观缺陷和性能不合格,在这里探讨的是外观缺陷。外观缺陷大多与生产工艺、原材料质嚣、生产设备、生产环境等因素有关。常见的缺陷有长条、连粒、黑点、变色、真空不良、铁屑、塑化不良、碳化等。文章从生产过程入手,对改性塑料常见的质量问题进行分析并提出对策。 二、常见缺陷 < |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |