牌号简介 About |
---|
Braskem PE_sha7260 sha7260是一种高密度聚乙烯,开发用于注塑成型,易于加工,生产率高。该树脂具有良好的熔体流动性,硬度高。其较窄的摩尔质量分布导致较低的翘曲倾向。该等级的最低生物基含量为94.5%,根据ASTM D6866测定。用途:桶、盆、瓶盖、瓶盖、玩具、盖子、薄壁零件和家庭用品。化妆品和药品应用的刚性容器(符合USP 37)Braskem PE Sha7260说明:Sha7260是一种高密度聚乙烯,开发用于注塑成型,易于加工,生产率高。该树脂具有良好的熔体流动性,硬度高。其较窄的摩尔质量分布导致较低的翘曲倾向。该等级的最低生物基含量为94%,根据ASTM D6866测定。用途:桶、盆、瓶盖、瓶盖、玩具、盖子、薄壁零件和家庭用品。 Braskem PE SHA7260 SHA7260 is a high-density polyethylene, developed for the injection molding, easy to process and with high productivity. This resin has a good melt flow with high rigidity and hardness. Its narrow molar mass distribution results in a low tendency to warpage. The minimum biobased content of this grade is 94%, determined according to ASTM D6866. Application: Pails & basins, Caps & Closures, Toys, Lids, Thin-walled parts and Housewares. Rigid containers for cosmetics and pharmaceutical applications (complies with USP 37). Process: Injection Molding Braskem PE SHA7260 SHA7260 is a high-density polyethylene, developed for the injection molding, easy to process and with high productivity. This resin has a good melt flow with high rigidity and hardness. Its narrow molar mass distribution results in a low tendency to warpage. The minimum biobased content of this grade is 94%, determined according to ASTM D6866. Application: Pails & basins, Caps & Closures, Toys, Lids, Thin-walled parts and Housewares. Rigid containers for cosmetics and pharmaceutical applications (complies with USP 37). Process: Injection Molding |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.955 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
20 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
50 ℃,2.00 mm,100%非离子表面活性剂,模压成型,F50 50 ℃, 2.00 mm, 100% non-ionic surfactant, molded, F50 |
< 4.00 | hr | ASTM D1693 |
Biobased Content Biobased Content |
94 | % | ASTM D6866 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
64 | ASTM D2240 | |
拉伸强度 tensile strength |
|||
屈服,模压成型 Yield, molding |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
屈服,模压成型 Yield, molding |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
1% 正割,模压成型 1% cut, molded |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
模压成型 Compression Molding |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,模压成型 0.45 MPa, unannealed, molded |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
沙特根底携手韩国SK化学进军LDPE、POEs和POPs业务
2016-07-07 沙特基础工业公司将在即将到来的十月份的K2016展示新材料和应用,成为其新的茂金属基聚烯烃特殊弹性体和塑性体(POE / POP)共聚物;这一成果是和韩国SK环球化工共同完成的。这使得沙特基础工业跻身专注塑料改性和薄膜应用的业务板块。这一市场的参与者屈指可数:密歇根州的陶氏化学,休斯敦的埃克森美孚公司与旗下的Exact和威达美树脂;新加坡三井弹性体;韩国的LG化学和其新的Lucene POE品牌。 50-50的合资公司,SSNC公司总部设在新加坡。沙特工业收购了SK Nex |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |