牌号简介 About |
---|
非常高的耐热性abs iso shortname:iso 2580-1 abs 2-m,mg,115-08-09-20优点:增加流量超低排放等级非常高的维卡软化点abs等级适用于内部和外部应用注射成型加工应用中较低的铸模沉积物在热化学成分下的尺寸更好:丙烯腈苯乙烯-马来酰亚胺(SMI)改性丁二烯-苯乙烯共聚物 Very high heat resistance ABS ISO shortname: ISO 2580-1 ABS 2-M, MG, 115-08-09-20 Major Benefits: Increased flow Super low emission grade Very high vicat softening point ABS grade suitable for interior and exterior applications Lower mould deposits in injection molding processing applications Better dimensional under heat Chemical Composition: Acrylonitrile-butadiene-styrene (ABS) copolymer modified with poly(styrene-co-maleimide) (SMI) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
220℃,10 kg 220℃,10 kg |
9.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate 2 |
ISO 294-4 | ||
TD TD |
0.60 to 0.70 | % | ISO 294-4 |
MD MD |
0.60 to 0.70 | % | ISO 294-4 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
13 | kJ/m² | ISO 179/1eA |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
燃烧速率 Burning rate 4 |
|||
2.0 mm 2.0 mm 4 |
mm/min | ISO 3795 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 3 |
|||
23℃ 23℃ 3 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
|||
23℃ 23℃ |
MPa | ISO 178 | |
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2 |
3 0.079 in/min |
4 US - FMVSS |
【新闻资讯】查看全部
中国石化在新疆棉田完成耐候地膜回收实验
2021-04-19 搜料网资讯: 近日,一款长效耐候地膜在新疆阿克苏地区棉田使用240天后,完成回收实验,可实现重复利用,回收率显著优于同类产品,大幅减少塑料残膜对土地的污染,为棉田可持续 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |