牌号简介 About |
---|
符合/超过福特工程规范ESA-M4D166-A。主要用于风扇罩和电池盖。 Sindustris PBT HI2304 is a Polycarbonate + PBT (PC+PBT) material filled with 30% glass fiber. It is available in Asia Pacific for injection molding. Primary attribute of Sindustris PBT HI2304: Impact Resistant. Typical application of Sindustris PBT HI2304: Electrical/Electronic Applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.44 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.30 到 1.0 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂,3.20 mm Fracture, 3.20 mm 2 |
98.1 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂,3.20 mm Fracture, 3.20 mm 2 |
4.5 | % | ASTM D638 |
弯曲模量 Bending modulus 3 |
|||
3.20 mm 3.20 mm 3 |
6370 | MPa | ASTM D790 |
弯曲强度 bending strength 3 |
|||
3.20 mm 3.20 mm 3 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |