牌号简介 About |
---|
注塑级,高流量PPO/PA合金,说明GF 30%增强,高流量,高耐热性应用,电气和电子零件 Injection Molding Grade, High Flow PPO/PA Alloy Description GF 30% Reinforcement, High Flow, High Heat Resistance Application Electric and Electronic parts |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.34 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
285℃,5.0kg 285℃,5.0kg |
41 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
屈服,3.20 mm Yield, 3.20 mm 2 |
149 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂,3.20 mm Fracture, 3.20 mm 2 |
8.0 | % | ASTM D638 |
弯曲模量 Bending modulus 3 |
|||
3.20 mm 3.20 mm 3 |
6960 | MPa | ASTM D790 |
弯曲强度 bending strength 3 |
|||
断裂,3.20 mm Fracture, 3.20 mm 3 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 0.11 in/min |
【新闻资讯】查看全部
塑料瓶的包装或将暂时被市场看好
2015-11-30 生活中对于各类的瓶瓶罐罐,我们在用到最后的时候,用勺子刨感觉不值,直接丢弃又觉得可惜,真正的如鸡肋一般,丢留两为难。塑料瓶的包装长期被市场看好。 由于它具有质轻、坚固耐用、阻隔性好、易成型、形状多变、成本低廉等一系列优点,在包装行业中具有非常强的竞争力。自从塑料包装诞生到现在,它已经成为各种包装材料之首。其塑料包装塑料瓶需求量日趋增加,吹塑成型设备也在不断增长。 塑料包装材料主要分为薄膜和形塑两大类,是塑料制品应用中的最大领域之一,广泛应用于烟草、食品饮料、 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |