牌号简介 About |
---|
isplen PB110H2E是一种高熔体粘度的丙烯异相共聚物,具有为挤出工艺设计的增强配方。由于其良好的流动性和优异的机械性能,适合加工成管道,其良好的弯曲模量专门用于双波纹排水管和污水管的挤压,具有低温冲击强度高、抗应力开裂等特点的ISPLEN PB110H2E保证了良好的性能。临界条件下的材料强度。在挤出过程中,使用合适的颜料可以很容易地着色,最好是以浓缩物的形式,其熔体流动速率比基聚合物高。典型的应用结构双层壁管道用于地下排水和无压污水。波纹管一般。推荐的熔化温度范围为205-225°C。应优化每个生产线的加工条件。isplen pb 110 h2e是一种极低熔体流动丙烯异相共聚物,具有用于挤出工艺的增强配方和高热稳定性。他的晶体结构具有很高的刚性和很高的抗张强度。其流动特性和机械性能使其特别适用于高厚度和良好表面光泽的挤出产品。在挤出过程中,使用合适的颜料,最好是以比基聚合物具有更高熔融流速的浓缩物的形式,可以很容易地着色。在挤出过程中可能需要高熔体粘度和特别高拉伸性能的典型应用,例如:具有高表面光泽的板材和型材吹塑板挤出。管。推荐的熔化温度范围为190至250°C。应优化每个生产线的加工条件。 ISPLEN® PB110H2E is a high melt viscosity propylene heterophasic copolymer with a reinforced formulation designed for extrusion process. Due to their good flow and outstanding mechanical properties it is suitable to be processed into pipes and its good flexural modulus is specially intended for extrusion of doubled corrugated drainage and sewage pipes The ISPLEN® PB110H2E characterized by high impact strength at low temperatures and stress cracking resistance assure the good performance of this material under critical conditions. It can be easily coloured during the extrusion process using the right pigments, preferably in the form of concentrates with a higher melt flow rate than the base polymer. TYPICAL APPLICATIONS Structured doubled wall pipes for underground drainage and sewage without pressure. Corrugated pipes in general. Recommended melt temperature range from 205-225 °C. Processing conditions should be optimised for each production line. ISPLEN® PB 110 H2E is a very low melt flow propylene heterophasic copolymer with a reinforced formulation for extrusion processes, and a high thermal stabilisation. His crystalline structure gives a high rigidity and very high tensile strength resistance. Its flow characteristics and mechanical properties make it specially adapted for high thickness and good superficial shine extrusion products It can be easily coloured during the extrusion process using the right pigments, preferably in the form of concentrates with a higher melt flow rate than the base polymer. TYPICAL APPLICATIONS In extrusion process that may require high melt viscosity and particularly high tensile properties, such as: Boards and Profiles Blow-molding Sheet extrusion with high superficial shine. Pipes. Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
230℃,2.16kg 230℃,2.16kg |
0.30 | g/10min | ISO 1133 |
230℃,5.0kg 230℃,5.0kg |
1.2 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
62 | ISO 868 | |
弯曲模量 Bending modulus |
1200 to 1300 | MPa | ISO 178 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A120 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
日涨千元!EVA后发先至!
2021-03-19 搜料网资讯: 节后归来,中国塑料城价格牛气十足,PP、PE、ABS、PC、PA..... 各品种强势普涨,一波接一波的热浪,令人猝不及防,但就在这全线升温的大环境下,EVA却原地踏步显得格外 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |