聚丙烯均聚物,40%碳酸钙填充,耐清洁剂 Bayfit 566 is a water-blown (MDI)/polyether based foam system used to manufacture high resilience (HR) cold-cure flex molded foam with medium to high load bearing properties. This system is characterized by good flow behavior in a wide variety of parts. Applications include office furniture, recreational seating, armrests and cushions. Bayfit 566 foam made at indices ranging from 80 to 105 typically passes the requirements of CAL-117 for flame resistance. Foams made at higher indices typically do not. As with any product, use of the Bayfit 566 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.0449 | g/cm³ | ASTM D3574 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
0.0965 | MPa | ASTM D3574 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
110 | % | ASTM D3574 |
撕裂阻力 Tear resistance |
401.8 | g/2.5 cm | ASTM D3574 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩形变 Compression deformation |
ASTM D3574 | ||
50% 50% |
3.6 | % | ASTM D3574 |
70% 70% |
% | ASTM D3574 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
IFD IFD |
ASTM D3574 | ||
25% R:102 mm 25% R:102 mm |
lb/50 in² | ASTM D3574 | |
65% R:102 mm 65% R:102 mm |
lb/50 in² | ASTM D3574 | |
SAG Factor(65%/25% IFD) SAG Factor(65%/25% IFD) |
ASTM D3574 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
研讨员将纺织品嵌入3D打印以制造柔性功用部件
2017-07-05 核心提示:研究人员将设计直接3D打印到织物上,通过将织物夹在两层3D打印塑料之间,某些情况下则将织物嵌入两层3D打印塑料之间。 近日,来自卡内基梅隆大学和罗切斯特理工学院(RIT)的研究人员发表了一篇名为《用嵌入式纺织品延伸3D打印的界限》的论文,其中详细介绍了用3D打印机来制造更强 科技媒体3D打印网讯近日,来自卡内基梅隆大学和罗切斯特理工学院(RIT)的研究人员发表了一篇名为《用嵌入式纺织品延伸3D打印的界限》的论文,其中详细介绍了用3D打印机来制造更强 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |