牌号简介 About |
---|
模克隆GP片材是一种抛光表面,紫外线稳定,透明的聚碳酸酯产品。它具有卓越的冲击强度、卓越的尺寸稳定性、耐高温性和高清晰度。这种轻质热成型板也容易制造和装饰。模克隆GP表提供五(5)年的产品破损有限保修。保修条款可根据要求提供。应用工业玻璃、机械防护装置、结构件、热成型和装配部件 Makrolon® GP sheet is a polished surface, UV stabilized, transparent polycarbonate product. It features outstanding impact strength, superior dimensional stability, high temperature resistance, and high clarity. This lightweight thermoformable sheet is also easy to fabricate and decorate. Makrolon GP sheet is offered with a five (5) year Limited Product Warranty against breakage. The terms of the warranty are available upon request. Applications Industrial glazing, machine guards, structural parts, thermoformed and fabricated components |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.15 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
960 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
3.2 mm 3.2 mm |
无断裂 | ASTM D256 | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
3.18 mm 3.18 mm |
> 63.7 | J | ASTM D3763 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
遮阳系数 Sunshade coefficient |
NFRC 100-2010 | ||
Clear:5.99 mm Clear:5.99 mm |
NFRC 100-2010 | ||
Gray or Bronze:5.99 mm Gray or Bronze:5.99 mm |
NFRC 100-2010 | ||
U Factor U Factor |
NFRC 100-2010 | ||
Summer:5.99 mm Summer:5.99 mm |
BTU/hr/ft²/°F | NFRC 100-2010 | |
Summer:9.53 mm Summer:9.53 mm |
BTU/hr/ft²/°F | NFRC 100-2010 | |
Winter:5.99 mm Winter:5.99 mm |
BTU/hr/ft²/°F | NFRC 100-2010 | |
Winter:9.53 mm Winter:9.53 mm |
BTU/hr/ft²/°F | NFRC 100-2010 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
|||
3.18 mm,在空气中 3.18 mm in air |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
10 Hz 10 Hz |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
60 Hz 60 Hz |
ASTM D150 | ||
耐电弧性 Arc resistance |
ASTM D495 | ||
-- -- 5 |
sec | ASTM D495 | |
-- -- 6 |
sec | ASTM D495 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
10.00 mm 10.00 mm |
UL 94 | ||
Flash Ignition Temperature Flash Ignition Temperature |
℃ | ASTM D1929 | |
Horizontal Burn(AEB) Horizontal Burn(AEB) |
cm | ASTM D635 | |
自燃温度 Autoignition temperature |
℃ | ASTM D1929 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
ASTM D1003 | ||
3000 µm 3000 µm 7 |
% | ASTM D1003 | |
3000 µm 3000 µm 8 |
% | ASTM D1003 | |
3000 µm 3000 µm 10 |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
极限 limit |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切模量 shear modulus |
MPa | ASTM D732 | |
剪切强度 shear strength |
ASTM D732 | ||
-- -- 3 |
MPa | ASTM D732 | |
-- -- 4 |
MPa | ASTM D732 | |
泊松比 Poisson's ratio |
ASTM E132 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Yield |
3 Ultimate |
4 Tungsten Electrodes |
5 Steel Strip Electrode |
6 K09 Bronze |
7 I35 Dark Gray |
8 Clear |
9 I30 Gray |
【新闻资讯】查看全部
扬子石化实现茂金属聚乙烯产品工业化量产
2021-03-22 搜料网资讯: 自3月5日开始生产茂金属聚乙烯以来,经过优化运行,截至3月15日,扬子石化塑料厂10天已经累计生产出3000多吨茂金属聚乙烯管材料产品mPE P3806R,成功实现茂金属聚乙烯的 |
扬子石化实现茂金属聚乙烯产品工业化量产 搜料网资讯:自3月5日开始生产茂金属聚乙烯以来,经过优化运行,截至3月15日,扬子石化塑料厂10天已经累计生产出3000多吨茂金属聚乙烯管材料产品mPE P3806R,成功实现茂金属聚乙烯的工业化量产。
经过检验,此次生产的产品融指、密度及物性指标全部合格。并且,该公司首次成功探索出在冷凝模式下生产茂金属,有效提高了生产负荷。与上年度试生产情况相比,此次茂金属聚乙烯产品转产时间和过渡料均大幅减少,产品质量明显改善,转产和生产过程稳定,产量实现翻番。 作为中国石化集团公司顶替进口项目,扬子石化高度重视茂金属聚乙烯产品的研究与开发,进行了长期跟踪和研究探索。科研部门凭借自身的技术优势,先后在聚烯烃小试和中试装置上开展了一系列试验工作,并在此基础上着力加快茂金属产品的工业化进程,提供整套工艺包技术,塑料厂2019年和2020年分别进行了两次试生产,积累了大量生产经验,产品经过下游用户使用后得到认可,满足了国内高端市场的需求。 茂金属聚乙烯系列产品开发生产,是扬子石化塑料产品结构调整优化工作的关键一环,也是攻坚创效的重头戏。作为高端聚乙烯产品,其应用领域十分广阔,以其制成的薄膜产品具有更高的强度和更好的耐穿刺性能,所制成的管材产品,抗蠕变性能更好,耐压等级更高,由于其卓越的力学性能和优异的光学性能,产品备受下游客户的青睐,目前,受技术和生产难度制约,国内仅有少数企业具备生产能力,市场基本依赖进口。 由于茂金属催化剂对杂质极为敏感,稍有不慎,极有可能导致生产失败,所以此次放量生产,聚乙烯车间提前进行了装置清理检修,为茂金属产品生产创造条件。为了保证茂金属催化剂使用的活性,并且避免产生晶点,聚乙烯车间从精制系统再生、干粉加料器清理调试、循环气管线射流清理,到反应器分布板内壁清理、滤袋更换、脱气仓清理检查,车间干部员工发扬钉钉子精神,生产过程中,严格执行两规一卡,精心操作,紧盯产品各项指标,克服生产过程中加料扰动、反应温度波动、己烯、氢气共聚互相干扰等一系列难点,终于成功生产出合格茂金属聚乙烯产品。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。