牌号简介 About |
---|
性能径向嵌段共聚物高强度低粘度高拉伸强度沥青混合料应用改性剂塑料改性鞋底改性 Styrene - Butadiene block copolymer designed for asphalt modification, solvent based adhesives, and for compounding applications. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
80 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
19.6 | MPa | ASTM D412 |
300% 应变 300% strain |
2.94 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
700 | % | ASTM D412 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
BD/SM Ratio BD/SM Ratio |
67/33 % | ASTM D1416 | |
Diblock Content Diblock Content |
% | ASTM D5296 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
Block Styrene Block Styrene |
% | ASTM D3314 | |
灰份含量 Ash Content |
% | ASTM D1416 | |
挥发物 Volatiles |
% | ASTM D1416 | |
布络克菲尔德粘度 Brookfield viscosity |
Pa·s | ASTM D1084 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
注塑模具顶针断裂缘由剖析
2018-09-30 一、顶针布置原则 (1)顶针布置应使顶出力尽量平衡。结构复杂部位所需脱模力较大,顶针数量应相应增加。 (2)顶针应设置于有效部位,如骨位、柱位、台阶、金属嵌件、局部厚胶等结构复杂部位。骨位、柱位两侧的顶针应尽量对称布置,顶针与骨位、柱位的边间距一般取D=1.5mm,如图5.5.8所示,另外,应尽量保证柱位两侧顶针的中心连线通过柱位中心。 (3)避免跨台阶或在斜 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |