牌号简介 About |
---|
在为LLDPE设计的流延膜机上,Lotr_ne Q2018C可以在中等的挤出压力、良好的纸幅稳定性和厚度控制下以最佳的输出速率进行加工。Lotr_ne Q2018c可与LDPE或其他用于铸膜单挤出或共挤出的PE树脂有利地混合,以改善薄膜性能。Lotr_ne Q2018c适用于消费、工业、食品或卫生包装领域的许多应用,以及拉伸膜和农业膜(如覆盖膜)等非包装应用。 Lotrène® Q2018C can be processed at optimal output rates with moderate extrusion pressure, good web stability and gauge control on cast film machines designed for LLDPE. Lotrène® Q2018C can advantageously be blended with LDPE or other PE resins used in cast film mono extrusion or co-extrusion to improve film properties. Lotrène® Q2018C is suited for many applications in the field of consumer, industrial, food or hygiene packaging as well as stretch film and non-packaging applications like agricultural films e.g. mulching films. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
膜刺穿强度 Membrane puncture strength |
|||
20 µm 20 µm |
1.60 | J | ASTM D5748 |
膜刺穿力 Membrane puncture force |
|||
20 µm 20 µm |
25.0 | N | ASTM D5748 |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:20 µm,铸造薄膜 1% secant, MD: 20 µ m, cast thin film |
165 | MPa | ASTM D882 |
1% 正割,TD:20 µm,铸造薄膜 1% secant, TD: 20 µ m, cast thin film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,20 µm,吹塑薄膜 MD, yield, 20 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,20 µm,吹塑薄膜 TD, yield, 20 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,20 µm,吹塑薄膜 MD, fracture, 20 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,20 µm,吹塑薄膜 TD, fracture, 20 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,20 µm,挤塑薄膜 MD, fracture, 20 µ m, extruded film |
% | ASTM D882 | |
TD,断裂,20 µm,挤塑薄膜 TD, fracture, 20 µ m, extruded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
|||
20 µm,铸造薄膜 20 µ m, cast thin film 2 |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:20 µm,铸造薄膜 MD: 20 µ m, cast thin film |
g | ASTM D1922 | |
TD:20 µm,铸造薄膜 TD: 20 µ m, cast thin film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
熔融峰值温度 Melting peak temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,20 µm,铸造薄膜 45 °, 20 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
挤出速率 Extrusion rate |
m/sec |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
3 标准 B (120°C/h), 压 力1 (10N) |
【新闻资讯】查看全部
推进城市转型中国尼龙城树立成为重要载体
2019-02-14 “为推进资源型城市转型发展,我市把中国尼龙城建设作为重要载体,集中力量加快推进,今年要全力实施‘三大突破’,持续推动千亿级尼龙产业基地建设。”近日,平顶山市工信局局长史长现说。 推动项目建设实现大突破。今年,中国尼龙城建设共谋划重大项目17个,总投资186亿元。其中,计划建成投资26亿元的二期20万吨/年己内酰胺、投资6.3亿元的一期4万吨/年尼龙6民用丝工程等7个项目,总投资44亿元;续建投资8亿元的二期6万吨/年尼龙6民用丝、投资3亿元的二期7000万瓶/年聚氨酯泡沫填 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |