牌号简介 About |
---|
Alcudia PE045/A是一种低密度聚乙烯级产品,采用高压高压釜技术生产,适用于吹塑或铸膜应用。这种材料易于加工,滑动平衡性好,具有机械和光学性能,并且具有良好的拉伸性能。它含有抗静电、防滑和防堵塞添加剂。一般包装膜的典型应用。用粘合剂层压的薄膜。自动包装用薄膜。高清晰度,中高滑膜。建议的熔化温度范围为150至180°C。应优化每条生产线的加工条件。 ALCUDIA® PE045/A is a low density polyethylene grade, produced by high pressure autoclave technology, suitable for blown or cast film applications. This material offers easy processability, good balance of slip, mechanical and optical properties and excellent draw down. It contains antistatic, slip and antiblock additives. TYPICAL APPLICATIONS General packaging film. Film for lamination with adhesives. Film for automated packaging. High clarity, medium-high slip film. Recommended melt temperature range from 150 to 180°C. Processing conditions should be optimised for each production line. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
与自身 - 动态,吹塑薄膜 Self dynamic, blow molded film |
0.12 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
30 | µm | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,30 µm,吹塑薄膜 MD, yield, 30 µ m, blow molded film |
11.0 | MPa | ISO 527-3 |
TD,屈服,30 µm,吹塑薄膜 TD, yield, 30 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,30 µm,吹塑薄膜 MD : Break, 1.2 mil, Blown Film |
MPa | ISO 527-3 | |
TD,断裂,30 µm,吹塑薄膜 TD, fracture, 30 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,30 µm,吹塑薄膜 MD : Break, 1.2 mil, Blown Film |
% | ISO 527-3 | |
TD,断裂,30 µm,吹塑薄膜 TD, fracture, 30 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
30 µm,吹塑薄膜 30 µ m, blow molded film |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
MD:30 µm,吹塑薄膜 MD: 30 µ m, blow molded film |
N | ISO 6383-2 | |
TD:30 µm,吹塑薄膜 TD: 30 µ m, blow molded film |
N | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,30 µm,吹塑薄膜 45 °, 30 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
30 µm,吹塑薄膜 30 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
第十七届中国专利奖颁奖大会在北京举行
2015-12-17 12月15日上午,第十七届中国专利奖颁奖大会在北京举行,中塑协的6家会员单位有7项专利喜获表彰。他们分别是:杭州福膜新材料科技有限公司的“一种聚偏氟乙烯薄膜专用料”专利、大连实德科技发展有限公司的“自增强型塑料异型材及其生产方法”专利、广东邦宝益智玩具股份有限公司的“一种拼插式玩具的插接结构”专利、金发科技股份有限公司的“一种汽车用低TVOC聚丙烯组合物及其制备方法”和“一种聚酰胺6复合材料及其制备方法”专利、好孩子儿童用品有限公司的“儿童推车(D340)”专利、新疆蓝山屯河聚酯有限公司的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |