牌号简介 About |
---|
FRIANYL® A3 V2XI是一种未填充的聚酰胺66(尼龙66)化合物,含卤素阻燃剂,不含三氧化二锑、PBB和PBDE,UL列出的V2。经VDE认证。该化合物用于注塑成型。FRIANYL® A3 V2XI主要为电气和电子工业设计。它也适用于汽车或工业和消费者应用。 FRIANYL® A3 V2XI is an unfilled Polyamide 66 (Nylon 66) compound, flame retardant with halogens, free from antimony trioxide, PBB and PBDE, UL listed V2. It is VDE certified. This compound is intended for injection molding. FRIANYL® A3 V2XI is primarily designed for the Electrical and Electronic industry. It is also suitable for Automotive or Industrial & Consumer applications. |
产品描述 Product Description
厂家:美国塞拉尼斯 Celanese
类别:PA66 PA66
用途:汽车领域的应用;电气/电子应用领域;工业应用;消费品应用领域;
加工条件:注射成型 Injection Molding
性能特点: 卤化; 无锑; 防火阻燃等级V-2; 阻燃; Flame Characteristics,No antimony,Halogenated,V-2
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.28 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:23℃ TD:23℃ |
1.0 | % | ISO 294-4 |
MD:23℃ MD:23℃ |
1.0 | % | ISO 294-4 |
吸水率 Water absorption rate |
ISO 62 | ||
23℃,24hr 23℃,24hr |
1.0 | % | ISO 62 |
饱和,23℃ Saturation, 23 ℃ |
6.0 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-A | |
23℃ 23℃ |
kJ/m² | ISO 180-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
连续使用温度 Continuous use temperature 3 |
℃ | IEC 60216 | |
球压测试 Ball pressure test |
IEC 60695-10-2 | ||
125℃ 125℃ |
IEC 60695-10-2 | ||
165℃ 165℃ |
IEC 60695-10-2 | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity 4 |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
2 mm 2 mm |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
3.20 mm,解决方案 A 3.20 mm, solution A |
V | IEC 60112 | |
针焰测试 Needle flame test |
IEC 60695-11-5 | ||
1.00 mm 1.00 mm |
IEC 60695-11-5 | ||
2.00 mm 2.00 mm |
IEC 60695-11-5 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.80 mm 0.80 mm |
℃ | IEC 60695-2-12 | |
3.2 mm 3.2 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.8 mm 0.8 mm |
℃ | IEC 60695-2-13 | |
3.2 mm 3.2 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20000 hr |
3 23°C |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
原厂数据及认证:
抱歉!该牌号暂无认证数据。
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。