牌号简介 About |
---|
Capilene E 65 F是一种聚丙烯均聚物,适用于双向拉伸聚丙烯(BOPP)薄膜应用。产品特点:加工性好,薄膜拉伸性好,机械性能好,不含硬脂酸钙、滑脱剂和防堵剂。用途:适用于BOPP普通或共挤包装薄膜、金属化BOPP薄膜;挤出和共挤热成型。 CAPILENE® E 65 F is a polypropylene homopolymer intended for biaxially oriented polypropylene (BOPP) film applications. CAPILENE® E 65 F features: good processability, easy film stretchability and good mechanical properties; does not contain calcium stearate, slip and anti-blocking additives. Applications CAPILENE® E 65 F is suitable for: BOPP plain or coextruded packaging films, metallizable BOPP film; extrusion and coextrusion thermoforming. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
2.0 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
33.0 | MPa | ISO 527-2/50 |
拉伸应变 Tensile strain |
|||
屈服 yield |
15 | % | ISO 527-2/50 |
弯曲模量 Bending modulus 2 |
1450 | MPa | ISO 178 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
3.5 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
【新闻资讯】查看全部
道达尔石化和炼油美国公司推出了高密度聚乙烯
2017-03-17 近期,道达尔石化和炼油美国公司推出了高密度聚乙烯。 相比其他应用于板材挤出热成型市场的HDPE,硬度的强化使这款材料在保持基本性能的同时,更能实现轻量化。或者客户可以选择生产相同重量的一款产品,但性能有所提高。 9825E具备的其他性能优势还包括高抗冲强度、耐化学性和水蒸气透过率低。 道达尔聚合物美州公司市场经理Ted Harris指出,“相比其他应用于热成型容器的HDPE,9825E不仅能提高硬度和加工性能,而且光泽度更好,能够改善产品的视 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |