牌号简介 About |
---|
LLBF-0822D是一种具有丁烯共聚单体的经认证的主要树脂,设计用于生产一般用途包装中使用的吹塑薄膜。LLBF-0822D具有工艺性好、薄膜强度好、热封温度范围宽等优点。LLBF-0822D的应用包括服装袋,衬里,生产袋和通用薄膜。LLBF-0822D含有中滑和高抗阻。LLBF-0822D符合FDA法规21CFR 177.1520(c)3.2A和大多数有关在食品接触中使用聚乙烯的国际法规。 LLBF-0822D is a certified prime resin with Butene-comonomer, designed for production of Blown films used in general purpose packaging. LLBF-0822D features excellent combination of easy processability with good film strength as well as wide heat sealing temperature range. LLBF-0822D applications include garment bags, liners, produce bags and general purpose films. LLBF-0822D contains medium slip and high antiblock. LLBF-0822D complies with FDA regulation 21CFR 177.1520(c)3.2a and with most international regulations concerning the use of Polyethylene in contact with food articles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.922 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
割线模量 Secant modulus |
|||
1% 正割,TD,25 µm 1% secant, TD, 25 µ m |
228 | MPa | ASTM D882 |
1% 正割,MD,25 µm 1% secant, MD, 25 µ m |
210 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,断裂,25 µm TD, fracture, 25 µ m |
MPa | ASTM D882 | |
TD,屈服,25 µm TD, yield, 25 µ m |
MPa | ASTM D882 | |
MD,断裂,25 µm MD, fracture, 25 µ m |
MPa | ASTM D882 | |
MD,屈服,25 µm MD, yield, 25 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,25 µm TD, fracture, 25 µ m |
% | ASTM D882 | |
MD,断裂,25 µm MD, fracture, 25 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 2 |
|||
25 µm 25 µm 2 |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD,25 µm MD,25 µm |
g | ASTM D1922 | |
撕裂强度 tear strength |
|||
TD,25 µm TD,25 µm |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25.4 µm,吹塑薄膜 45 °, 25.4 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25.4 µm,吹塑薄膜 25.4 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
“限塑令”施行成摆设 塑料制品累计增幅超3%
2017-07-26 为了响应减少塑料制品带来的“白色污染”,我国出台“限塑令”,但目前来看,‘限塑令’并没有达到预期。多地调查显示,塑料制品的使用量不降反增,随着快递行业和外卖行业迅猛发展,塑料包装的消耗也不断增多。 参考《中国塑料制品行业产销需求与投资预测分析报告》整理数据显示,2017年5月我国塑料制品产量674.6万吨,同比增长3%,1-5月累计产量3047万吨,累计增长3.8%。 以下为2016年6月至2017年5月我国塑料制品产量统计: 另一方面,中国 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |