牌号简介 About |
---|
Pocan T 7323 000000 PBT+PET,20%玻璃纤维,注塑,改善表面光洁度,提高温度峰值负荷 POCAN® T7323 000000 PBT+PET, 20 % glass fibers, injection molding, improved surface finish, increased temperature peak load POCAN® T7323 000000 PBT+PET, 20 % glass fibers, injection molding, improved surface finish, increased temperature peak load POCAN® T7323 000000 PBT+PET, 20 % glass fibers, injection molding, improved surface finish, increased temperature peak load |
产品描述 Product Description
厂家:德国朗盛 LANXESS
类别:PBT+PET PBT+PET
加工条件:注射成型 Injection Molding
性能特点: 耐热性好; 防火阻燃等级HB; 耐高温; 耐候抗UV; 表面光泽度好; Weather resistance is good,Good surface appearance,High Heat Resistance,Heat Resistance, Good,HB
填料:玻璃纤维 20
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.47 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.80 | g/cm³ | ISO 60 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,2.16 kg 260℃,2.16 kg |
15.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:270℃,2.0 mm TD:270℃,2.0 mm 2 |
1.0 | % | ISO 294-4 |
TD:120℃,2.0 mm,2 hrs TD:120℃,2.0 mm,2 hrs 3 |
0.20 | % | ISO 294-4 |
MD:270℃,2.0 mm MD:270℃,2.0 mm 2 |
% | ISO 294-4 | |
MD:120℃,2.0 mm,2 hrs MD:120℃,2.0 mm,2 hrs 3 |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
粘度值 Viscosity value |
|||
降低的粘度 Reduced viscosity |
ml/g | ISO 1628 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-40℃ -40℃ |
kJ/m² | ISO 180-1A | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
球压测试 Ball pressure test |
|||
215℃ 215℃ |
IEC 60695-10-2 | ||
熔融温度 Melting temperature 5 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
|||
23℃ 23℃ |
W/m/K | ISO 8302 | |
Halving Interval Halving Interval |
IEC 60216 | ||
-- -- 7 |
℃ | IEC 60216 | |
1.50 mm 1.50 mm 8 |
℃ | IEC 60216 | |
1.50 mm 1.50 mm 9 |
℃ | IEC 60216 | |
温度指数 Temperature index 10 |
IEC 60216 | ||
介电强度 Dielectric strength |
IEC 60216 | ||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
拉伸冲击强度:1.50 mm Tensile impact strength: 1.50 mm |
IEC 60216 | ||
拉伸强度:1.50 mm Tensile strength: 1.50 mm |
IEC 60216 | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index 11 |
% | ISO 4589-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
IEC 60426 | ||
ISO Shortname ISO Shortname |
ISO 7792 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲强度 bending strength 4 |
|||
3.50% 应变 3.50% strain |
MPa | ISO 178-A | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Bending strain 5 |
% | ||
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2mm, 90°C MT, 600 bar |
3 60x60x2; MT 90°C; 600 Bar |
4 60x60x2 |
5 60x60x2mm |
6 0.079 in/min |
7 Pull Rate: 2 mm/min; 50% RH |
8 2 mm/min |
9 10°C/min |
10 Electric Strength |
11 Tensile Strength |
12 Tensile Impact Strength |
13 20000 h |
14 程序 A |
【新闻资讯】查看全部
原油价格飙升,欧佩克+消息来源显示产量维持稳定
2021-03-05 搜料网资讯: 美国原油基准WTI原油周四早盘跳升至64美元/桶上方,飙升幅度超过5%,此前欧佩克+消息人士称,该联盟近乎同意不在4月集体增加原油产量。 截至美国东部时间周四上午1 |
原油价格飙升,欧佩克+消息来源显示产量维持稳定 搜料网资讯:美国原油基准WTI原油周四早盘跳升至64美元/桶上方,飙升幅度超过5%,此前欧佩克+消息人士称,该联盟近乎同意不在4月集体增加原油产量。
截至美国东部时间周四上午11:18,WTI原油价格大涨5.06%,报64.21美元。在欧佩克+消息人士开始从正在举行的欧佩克+部长级会议中泄露消息后,布伦特原油价格跳涨至67美元/桶上方,至67.17美元,涨幅为5.10%。 据与会代表表示,目前讨论的是除俄罗斯和哈萨克斯坦之外的所有成员国的产量展期问题。能源情报局副局长兼欧佩克首席记者阿蒙娜·巴克尔(Amena Bakr)在推特上说:“这两个国家将被允许分别增加13万和2万桶产量。” 据报道,作为欧佩克最大的产油国和事实上的领导者,沙特阿拉伯提议将目前的减产水平延续到4月和5月。此外,沙特也将在4月保留其额外的100万桶/日减产计划。该额外减产最初计划只在2月和3月持续。 俄罗斯和哈萨克斯坦都在推动提高集体产量。俄罗斯是欧佩克+协议中非欧佩克成员国集团的领导者,据报道,俄罗斯正在推动在4月份获得增产,以满足国内燃料的高需求。 然而,正如预期的那样,沙特阿拉伯呼吁采取更加“谨慎”的态度。沙特能源部长阿卜杜拉齐兹·本·萨勒曼亲王在会上说:“虽然已是老生常谈,但我要再次呼吁大家保持谨慎和警惕。在我们采取下一步行动之前,让我们先确定我们看到的前方的光亮不是迎面而来的快车的车灯。” |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。