牌号简介 About |
---|
Pocan S 1506 000000 PBT,非增强,注塑,挤压,提高冲击强度,Pocan S 1506 000000 PBT,非增强,注塑挤出,提高冲击强度 POCAN® S1506 000000 PBT, non-reinforced, injection molding, extrusion, improved impact strength POCAN® S1506 000000 PBT, non-reinforced, injection molding, extrusion, improved impact strength POCAN® S1506 000000 PBT, non-reinforced, injection molding, extrusion, improved impact strength |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.70 | g/cm³ | ISO 60 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,5 kg 260℃,5 kg |
14.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:260℃,2.0 mm TD:260℃,2.0 mm 2 |
1.8 | % | ISO 294-4 |
TD:120℃,2.0 mm,2 hrs TD:120℃,2.0 mm,2 hrs 3 |
0.40 | % | ISO 294-4 |
MD:260℃,2.0 mm MD:260℃,2.0 mm 2 |
% | ISO 294-4 | |
MD:120℃,2.0 mm,2 hrs MD:120℃,2.0 mm,2 hrs 3 |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
ISO 6603-2 | ||
-30℃ -30℃ |
N | ISO 6603-2 | |
23℃ 23℃ |
N | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
180℃ 180℃ |
IEC 60695-10-2 | ||
熔融温度 Melting temperature 5 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
|||
23℃ 23℃ |
W/m/K | ISO 8302 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index 7 |
% | ISO 4589-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
IEC 60426 | ||
ISO Shortname ISO Shortname |
ISO 7792 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2/50 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲强度 bending strength 4 |
|||
3.50% 应变 3.50% strain |
MPa | ISO 178-A | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Bending strain 5 |
% | ||
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2mm, 80°C MT, 600 bar |
3 60x60x2; MT 80°C; 600 Bar |
4 60x60x2 |
5 60x60x2mm |
6 0.079 in/min |
7 2 mm/min |
8 Pull Rate: 2 mm/min; 50% RH |
9 10°C/min |
10 程序 A |
【新闻资讯】查看全部
柔宇和三星区分发布了可折叠屏幕的手机
2019-01-08 今年10、11月份,柔宇科技和三星公司分别发布了可折叠屏幕的手机。与普通“硬邦邦”的智能手机不通,可折叠手机采用了柔性显示触摸幕,消费者可轻松进行弯折和扭曲! 有分析报告指出,柔性显示幕目前主要是用聚酰亚胺(Polyimide,简称PI)代替玻璃来做基板,从而使得屏幕变得可弯曲,变硬屏为软屏。 |
柔宇和三星区分发布了可折叠屏幕的手机 今年10、11月份,柔宇科技和三星公司分别发布了可折叠屏幕的手机。与普通“硬邦邦”的智能手机不通,可折叠手机采用了柔性显示触摸幕,消费者可轻松进行弯折和扭曲! 有分析报告指出,柔性显示幕目前主要是用聚酰亚胺(Polyimide,简称PI)代替玻璃来做基板,从而使得屏幕变得可弯曲,变硬屏为软屏。 聚酰亚胺(PI)是一类分子链中含有环状酰亚胺基团的高分子聚合物。它具有优异的耐高温、耐低温、高强高模、高抗蠕变、高尺寸稳定、低热膨胀系数、高电绝缘、低介电常数与低损耗、耐辐射、耐腐蚀等优点。 同时,其具有真空挥发份低、挥发可凝物少等空间材料的特点,可加工成聚酰亚胺薄膜、耐高温工程塑料、复合材料用基体树脂、耐高温粘结剂、纤维和泡沫等多种材料形式。 近年来,各国都在研究、开发及利用聚酰亚胺,并将聚酰亚胺列为“21世纪最有希望的工程塑料”之一。鉴于其优异的性能,又被称为是“解决问题的能手”,人们普遍认为“没有聚酰亚胺就不会有今天的微电子技术”。 聚酰亚胺产品以薄膜、涂料、纤维、工程塑料、复合材料、胶粘剂、泡沫塑料、分离膜、液晶取向剂、光刻胶等为主,可应用到航空航天、电气绝缘、液晶显示、汽车医疗、原子能、卫星、核潜艇、微电子、精密机械包装等。 其中,聚酰亚胺薄膜为聚酰亚胺系列产品中应用最早,最为成熟的产品。电子级以下聚酰亚胺薄膜已实现国产自给自足,电子级及以上聚酰亚胺薄膜市场仍主要由海外公司瓜分。 高端聚酰亚胺薄膜技术仍为少数国外企业垄断 随着柔性显示幕的快速发展,高端电子级的聚酰亚胺薄膜市场将处于快速扩张期。据美国调查咨询公司 Markets and Markets资料显示,2017年全球聚酰亚胺薄膜的市场规模为15.2亿美元,预计2022年将达到24.5亿美元。 聚酰亚胺技术在世界范围内呈寡头垄断局面,技术封锁严密。聚酰亚胺薄膜发展较好,拥有技术的巨头企业较多,但聚酰亚胺薄膜仍属于高技术壁垒行业。 目前全球产能仍然主要由国外少数企业所垄断,包括美国杜邦、钟渊化学(Kaneka)、韩国SKPI以及日本宇部兴产株式会社(UBE)等。 宇部兴产在2018年第二季度财报(截至2018年6月30日)中指出,得益于聚酰亚胺业务的重建,公司今年第二季度的PI净销售额与2018年同期相比,实现了强劲增长,主要受益于OLED柔性显示幕的市场增长。宇部兴产还将研发新的PI薄膜牌号,以提高电路板(FPC)市场占有率并扩大销售双面COF 薄膜。 中国聚酰亚胺进口依赖度达41.6% 中国在聚酰亚胺薄膜产业化方面起步并不晚,早在上世纪70年代就由原一机部组织开展了聚酰亚胺薄膜制造技术的研究。但由于种种原因,中国高性能聚酰亚胺薄膜的制造技术一直处于低水准徘徊的状态。 上世纪90年代后期,伴随着超大型积体电路制造与封装产业和特种电力电器行业等的高速发展,高性能聚酰亚胺薄膜材料的匮乏,成为严重制约中国高新技术产业发展的瓶颈。 面对中国聚酰亚胺薄膜急需解决的科学和技术难题,中国科学院化学研究所自2003年起在国家发改委国家高技术产业化项目的支持下,与深圳瑞华泰薄膜科技有限公司合作,开始致力于高性能聚酰亚胺薄膜制造技术的研究。 通过近八年的努力,攻克了从关键树脂制备到连续双向拉伸聚酰亚胺薄膜生产的稳定工艺等技术关键,掌握了具有自主智慧财产权的高性能聚酰亚胺薄膜制造技术。 在此基础上,于2010年建成中国规模最大的高性能聚酰亚胺薄膜生产基地,第一期项目建设共计投入118亿元人民币,完成3条1200mm幅宽双向拉伸工艺技术的高性能聚酰亚胺薄膜连续化生产线的建设,满负荷年生产能力达到350t。该生产基地的建成投产,打破了国外厂家在聚酰亚胺薄膜材料领域的垄断,加快了聚酰亚胺薄膜在航空航天、太阳能等高端应用领域的国产化进程。 来源:CPRJ中国塑料橡胶 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。