牌号简介 About |
---|
高耐热性ABS ISO 简称:iso 2580-1 abs 1-m,mg,105-15-16-20 优点:冲击强度和流动性的极好平衡超低排放级注塑加工中的低铸模沉积物应用在热下更好的尺寸化学成分:用聚乙烯改性的丙烯腈-丁二烯-苯乙烯(abs)共聚物(苯乙烯-马来酰亚胺)(SMI) High heat resistance ABS ISO shortname: ISO 2580-1 ABS 1-M, MG, 105-15-16-20 Major Benefits: Excellent balance of impact strength and flowability Super low emission grade Lower mould deposits in injection molding processing applications Better dimensional under heat Chemical Composition: Acrylonitrile-butadiene-styrene (ABS) copolymer modified with poly(styrene-co-maleimide) (SMI) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.03 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate Melt Volume Rate |
|||
220℃,10kg 220℃,10kg |
16 | cm³/10min | ISO 1133 |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
平行 parallel Parallel |
0.6-0.7 | % | ISO 294-4 |
法向 normal Normal |
0.6-0.7 | % | ISO 294-4 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 Tensile Strength Tensile Strength |
|||
屈服 yld Yield yld |
42 | MPa | ISO 527-2 |
断裂伸长率 Elongation at Break Elongation at Break |
% | ISO 527-1,2 | |
拉伸模量 Tensile Modulus Tensile Modulus |
MPa | ISO 527 | |
弯曲模量 Flexural Modulus Flexural Modulus |
MPa | ISO 178 | |
弯曲强度 Flexural Strength Flexural Strength |
MPa | ISO 178 | |
球压硬度 ball-indentation hardness Ball indentation hardness |
N/mm² | ISO 2039-1 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Izod Notched Impact strength Izod Notched Impact strength |
|||
23℃ 23℃ |
KJ/m² | ISO 180/1A | |
-30℃ -30℃ |
KJ/m² | ISO 180/1A | |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
kJ/m² | ISO 179/1eA | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
|||
B50, 50ºC/h B50, 50ºC/h |
℃ | ISO 306/B | |
B120, 120ºC/h B120, 120ºC/h |
℃ | ISO 306/B | |
热变形温度 HDT Hot deformation temperature HDT |
|||
1.80 MPa 1.80 MPa |
℃ | ISO 75-1/-2 | |
0.45 MPa 0.45 MPa |
℃ | ISO 75-1/-2 | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
平行 parallel Parallel |
×10-4/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
|||
1.6 mm 1.6 mm |
calss | UL 94 | |
FMVSS 阻燃等级 FMVSS flame retardant rating |
|||
200x105x2mm 200x105x2mm |
mm/min | ISO 3795 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2 |
3 0.079 in/min |
4 US - FMVSS |
【新闻资讯】查看全部
茂石化PPR-M55-S达国际抢先
2018-06-13 近日,茂名石化无规薄壁注塑聚丙烯等多种高端产品均实现了规模化量产,其中PPR-M55-S无规注塑产品关键指标国际领先,其优异的性能指标得益于该公司对新产品质量的不断优化。 PPR-M55-S属于高流动性高刚产品树脂,需要在高浓度氢气中加入乙烯反应,其熔融指数相当高,物料在挤压成型控制方面极其难控制,已达到装置挤压机运行的设计极限。 为提升该产品市场占有率,茂名石化组织研究院、化工分部技术质量处、聚丙烯车间技术骨干大力开展技术创新攻关,他们经过多次专题会议与技 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |