牌号简介 About |
---|
Texin 985U树脂是一种芳香族聚醚基热塑性聚氨酯,肖氏硬度约为85A,可通过注塑、挤出或吹塑加工。 Texin 985U resin is an aromatic polyether-based thermoplastic polyurethane with a Shore hardness of approximately 85A. It can be processed by injection molding, extrusion, or blow molding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.12 | g/cm³ | ASTM D792 |
密度 Density |
1.12 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 2577 | ||
TD:2.54 mm TD:2.54 mm |
0.80 | % | ASTM D955 |
MD:2.54 mm MD:2.54 mm |
0.80 | % | ASTM D955 |
TD:2.54 mm TD:2.54 mm |
0.80 | % | ISO 2577 |
MD:2.54 mm MD:2.54 mm |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
ASTM D2240 | ||
邵氏 A Shaw's A |
ISO 868 | ||
弯曲模量 Bending modulus |
ASTM D790 | ||
-30℃ -30℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
ISO 178 | ||
-30℃ -30℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ISO 4649 | |
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ASTM D1044 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 37 | |
屈服 yield |
MPa | ASTM D412 | |
300% 应变 300% strain |
MPa | ISO 37 | |
300% 应变 300% strain |
MPa | ASTM D412 | |
100% 应变 100% strain |
MPa | ASTM D412 | |
100% 应变 100% strain |
MPa | ISO 37 | |
50% 应变 50% strain |
MPa | ISO 37 | |
50% 应变 50% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 37 | |
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
撕裂强度 tear strength |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
ASTM D395B | ||
23℃,22 hr 23℃,22 hr 3 |
% | ASTM D395B | |
23℃,22 hr 23℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr 3 |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
压缩形变 Compression deformation |
ISO 815 | ||
23℃,22 hr 23℃,22 hr 3 |
% | ISO 815 | |
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr 3 |
% | ISO 815 | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
脆化温度 Embrittlement temperature |
℃ | ISO 974 | |
玻璃化转变温度 Glass transition temperature |
℃ | DMA | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/50 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ASTM D573 | ||
100℃,70 hr 100℃,70 hr |
% | ASTM D573 | |
100% Strain,100℃,70 hr 100% Strain,100℃,70 hr |
% | ASTM D573 | |
300% Strain,100℃,70 hr 300% Strain,100℃,70 hr |
% | ASTM D573 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
100% Strain,100℃,168 hr 100% Strain,100℃,168 hr |
% | ASTM D573 | |
300% Strain,100℃,168 hr 300% Strain,100℃,168 hr |
% | ASTM D573 | |
100℃,336 hr 100℃,336 hr |
% | ASTM D573 | |
100% Strain,100℃,336 hr 100% Strain,100℃,336 hr |
% | ASTM D573 | |
300% Strain,100℃,336 hr 300% Strain,100℃,336 hr |
% | ASTM D573 | |
100℃,504 hr 100℃,504 hr |
% | ASTM D573 | |
100% Strain,100℃,504 hr 100% Strain,100℃,504 hr |
% | ASTM D573 | |
300% Strain,100℃,504 hr 300% Strain,100℃,504 hr |
% | ASTM D573 | |
125℃,70 hr 125℃,70 hr |
% | ASTM D573 | |
100% Strain,125℃,70 hr 100% Strain,125℃,70 hr |
% | ASTM D573 | |
300% Strain,125℃,70 hr 300% Strain,125℃,70 hr |
% | ASTM D573 | |
125℃,168 hr 125℃,168 hr |
% | ASTM D573 | |
100% Strain,125℃,168 hr 100% Strain,125℃,168 hr |
% | ASTM D573 | |
300% Strain,125℃,168 hr 300% Strain,125℃,168 hr |
% | ASTM D573 | |
125℃,336 hr 125℃,336 hr |
% | ASTM D573 | |
100% Strain,125℃,336 hr 100% Strain,125℃,336 hr |
% | ASTM D573 | |
300% Strain,125℃,336 hr 300% Strain,125℃,336 hr |
% | ASTM D573 | |
125℃,504 hr 125℃,504 hr |
% | ASTM D573 | |
100% Strain,125℃,504 hr 100% Strain,125℃,504 hr |
% | ASTM D573 | |
300% Strain,125℃,504 hr 300% Strain,125℃,504 hr |
% | ASTM D573 | |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ISO 216 | ||
100℃,70 hr 100℃,70 hr |
% | ISO 216 | |
100% Strain 100℃,70 hr 100% Strain 100℃,70 hr |
% | ISO 216 | |
300% Strain 100℃,70 hr 300% Strain 100℃,70 hr |
% | ISO 216 | |
100℃,168 hr 100℃,168 hr |
% | ISO 216 | |
100% Strain 100℃,168 hr 100% Strain 100℃,168 hr |
% | ISO 216 | |
300% Strain 100℃,168 hr 300% Strain 100℃,168 hr |
% | ISO 216 | |
100℃,336 hr 100℃,336 hr |
% | ISO 216 | |
100% Strain 100℃,336 hr 100% Strain 100℃,336 hr |
% | ISO 216 | |
300% Strain 100℃,336 hr 300% Strain 100℃,336 hr |
% | ISO 216 | |
100℃,504 hr 100℃,504 hr |
% | ISO 216 | |
100% Strain 100℃,504 hr 100% Strain 100℃,504 hr |
% | ISO 216 | |
300% Strain 100℃,504 hr 300% Strain 100℃,504 hr |
% | ISO 216 | |
125℃,70 hr 125℃,70 hr |
% | ISO 216 | |
100% Strain 125℃,70 hr 100% Strain 125℃,70 hr |
% | ISO 216 | |
300% Strain 125℃,70 hr 300% Strain 125℃,70 hr |
% | ISO 216 | |
125℃,168 hr 125℃,168 hr |
% | ISO 216 | |
100% 应变 125℃,168 hr 100% strain 125 ℃, 168 hr |
% | ISO 216 | |
300% Strain 125℃,168 hr 300% Strain 125℃,168 hr |
% | ISO 216 | |
125℃,336 hr 125℃,336 hr |
% | ISO 216 | |
100% Strain 125℃,336 hr 100% Strain 125℃,336 hr |
% | ISO 216 | |
300% Strain 125℃,336 hr 300% Strain 125℃,336 hr |
% | ISO 216 | |
125℃,504 hr 125℃,504 hr |
% | ISO 216 | |
100% Strain 125℃,504 hr 100% Strain 125℃,504 hr |
% | ISO 216 | |
300% Strain 125℃,504 hr 300% Strain 125℃,504 hr |
% | ISO 216 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
ASTM D573 | ||
100℃,70 hr 100℃,70 hr |
% | ASTM D573 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
100℃,336 hr 100℃,336 hr |
% | ASTM D573 | |
100℃,504 hr 100℃,504 hr |
% | ASTM D573 | |
125℃,70 hr 125℃,70 hr |
% | ASTM D573 | |
125℃,168 hr 125℃,168 hr |
% | ASTM D573 | |
125℃,336 hr 125℃,336 hr |
% | ASTM D573 | |
125℃,504 hr 125℃,504 hr |
% | ASTM D573 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air |
ISO 216 | ||
100℃,70 hr 100℃,70 hr |
% | ISO 216 | |
100℃,168 hr 100℃,168 hr |
% | ISO 216 | |
100℃,336 hr 100℃,336 hr |
% | ISO 216 | |
100℃,504 hr 100℃,504 hr |
% | ISO 216 | |
125℃,70 hr 125℃,70 hr |
% | ISO 216 | |
125℃,168 hr 125℃,168 hr |
% | ISO 216 | |
125℃,336 hr 125℃,336 hr |
% | ISO 216 | |
125℃,504 hr 125℃,504 hr |
% | ISO 216 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 | ||
邵氏 D,100℃,70 hr Shore D, 100 ℃, 70 hr |
ASTM D573 | ||
邵氏 D,100℃,168 hr Shore D, 100 ℃, 168 hr |
ASTM D573 | ||
邵氏 D,100℃,336 hr Shore D, 100 ℃, 336 hr |
ASTM D573 | ||
邵氏 D,100℃,504 hr Shore D, 100 ℃, 504 hr |
ASTM D573 | ||
邵氏 D,125℃,70 hr Shore D, 125 ℃, 70 hr |
ASTM D573 | ||
支撐 D,125℃,168 hr Support D, 125 ℃, 168 hr |
ASTM D573 | ||
邵氏 D,125℃,336 hr Shaw's D, 125 ℃, 336 hr |
ASTM D573 | ||
邵氏 D,125℃,504 hr Shaw's D, 125 ℃, 504 hr |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 216 | ||
邵氏 D,100℃,70 hr Shore D, 100 ℃, 70 hr |
ISO 216 | ||
邵氏 D,100℃,168 hr Shore D, 100 ℃, 168 hr |
ISO 216 | ||
邵氏 D,100℃,336 hr Shore D, 100 ℃, 336 hr |
ISO 216 | ||
邵氏 D,100℃,504 hr Shore D, 100 ℃, 504 hr |
ISO 216 | ||
邵氏 D,125℃,70 hr Shore D, 125 ℃, 70 hr |
ISO 216 | ||
支撐 D,125℃,168 hr Support D, 125 ℃, 168 hr |
ISO 216 | ||
邵氏 D,125℃,336 hr Shaw's D, 125 ℃, 336 hr |
ISO 216 | ||
邵氏 D,125℃,504 hr Shaw's D, 125 ℃, 504 hr |
ISO 216 | ||
拉伸强度的变化率 The rate of change in tensile strength |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
100% Strain,23℃,70 hr,in Reference Fuel C 100% Strain,23℃,70 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,70 hr,in Reference Fuel C 300% Strain,23℃,70 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
100% Strain,23℃,168 hr,in Reference Fuel C 100% Strain,23℃,168 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,168 hr,in Reference Fuel C 300% Strain,23℃,168 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
100% Strain,23℃,336 hr,in Reference Fuel C 100% Strain,23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,336 hr,in Reference Fuel C 300% Strain,23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100% Strain,23℃,504 hr,in Reference Fuel C 100% Strain,23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
300% Strain,23℃,504 hr,in Reference Fuel C 300% Strain,23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100% Strain,100℃,70 hr,in ASTM #1 Oil 100% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,70 hr,in ASTM #1 Oil 300% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100% Strain,100℃,70 hr,in ASTM #3 Oil 100% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,70 hr,in ASTM #3 Oil 300% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,168 hr,in ASTM #1 Oil 100% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,168 hr,in ASTM #1 Oil 300% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,168 hr,in ASTM #3 Oil 100% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,168 hr,in ASTM #3 Oil 300% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,336 hr,in ASTM #1 Oil 100% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,336 hr,in ASTM #1 Oil 300% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,336 hr,in ASTM #3 Oil 100% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,336 hr,in ASTM #3 Oil 300% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100% Strain,100℃,504 hr,in ASTM #1 Oil 100% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
300% Strain,100℃,504 hr,in ASTM #1 Oil 300% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100% Strain,100℃,504 hr,in ASTM #3 Oil 100% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
300% Strain,100℃,504 hr,in ASTM #3 Oil 300% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
拉伸强度的变化率 The rate of change in tensile strength |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
100% Strain,23℃,70 hr,in Reference Fuel C 100% Strain,23℃,70 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,70 hr,in Reference Fuel C 300% Strain,23℃,70 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
100% Strain,23℃,168 hr,in Reference Fuel C 100% Strain,23℃,168 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,168 hr,in Reference Fuel C 300% Strain,23℃,168 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
100% Strain,23℃,336 hr,in Reference Fuel C 100% Strain,23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,336 hr,in Reference Fuel C 300% Strain,23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 100% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) 300% Strain,23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100% Strain,23℃,504 hr,in Reference Fuel C 100% Strain,23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
300% Strain,23℃,504 hr,in Reference Fuel C 300% Strain,23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100% Strain,100℃,70 hr,in ASTM #1 Oil 100% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,70 hr,in ASTM #1 Oil 300% Strain,100℃,70 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100% Strain,100℃,70 hr,in ASTM #3 Oil 100% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,70 hr,in ASTM #3 Oil 300% Strain,100℃,70 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,168 hr,in ASTM #1 Oil 100% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,168 hr,in ASTM #1 Oil 300% Strain,100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,168 hr,in ASTM #3 Oil 100% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,168 hr,in ASTM #3 Oil 300% Strain,100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,336 hr,in ASTM #1 Oil 100% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,336 hr,in ASTM #1 Oil 300% Strain,100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,336 hr,in ASTM #3 Oil 100% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,336 hr,in ASTM #3 Oil 300% Strain,100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100% Strain,100℃,504 hr,in ASTM #1 Oil 100% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
300% Strain,100℃,504 hr,in ASTM #1 Oil 300% Strain,100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
100% Strain,100℃,504 hr,in ASTM #3 Oil 100% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
300% Strain,100℃,504 hr,in ASTM #3 Oil 300% Strain,100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
极限伸长率的变化率 Change rate of ultimate elongation |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
断裂时拉伸应力变化 Changes in tensile stress during fracture |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A(Isooctane) 23℃,70 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A(Isooctane) 23℃,168 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A(Isooctane) 23℃,336 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A(Isooctane) 23℃,504 hr,in Reference Fuel A(Isooctane) |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
邵氏硬度的变化率 The rate of change in Shore hardness 2 |
ASTM D471 | ||
邵氏 D,23℃,70 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,70 hr,在基准燃料C中 Shore D, 23°C, 70 hr, in Reference Fuel C |
ASTM D471 | ||
邵氏 D,23℃,168 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,168 hr,在基准燃料中 Shore D, 23 ℃, 168 hr, in reference fuel |
ASTM D471 | ||
邵氏 D,23℃,336 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,336 hr,在基准燃料C中 Shore D, 23 ℃, 336 hr, in reference fuel C |
ASTM D471 | ||
邵氏 D,23℃,504 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane) |
ASTM D471 | ||
邵氏 D,23℃,504 hr,,在基准燃料C中 Shore D, 23 ℃, 504 hr, in reference fuel C |
ASTM D471 | ||
邵氏 D,100℃,70 hr,在ASTM #1油中 Shore D, 100°C, 70 hr, in ASTM #1 Oil |
ASTM D471 | ||
邵氏 D,100℃,70 hr,在ASTM #3油中 Shore D, 100 ℃, 70 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,168 hr,在ASTM #1油中 Shore D, 100°C, 168 hr, in ASTM #1 Oil |
ASTM D471 | ||
邵氏 D,100℃,168 hr,在ASTM #3油中 Shore D, 100 ℃, 168 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,336 hr,在ASTM #1油中 Shore D, 100 ℃, 336 hr, in ASTM # 1 oil |
ASTM D471 | ||
邵氏 D,100℃,336 hr,在ASTM #3油中 Shore D, 100 ℃, 336 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏 D,100℃,504 hr,在ASTM #1油中 Shore D, 100 ℃, 504 hr, in ASTM # 1 oil |
ASTM D471 | ||
邵氏 D,100℃,504 hr,在ASTM #3油中 Shore D, 100 ℃, 504 hr, in ASTM # 3 oil |
ASTM D471 | ||
邵氏硬度的变化率 The rate of change in Shore hardness |
ISO 175 | ||
邵氏 D,23℃,70 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 70 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,70 hr,在基准燃料C中 Shore D, 23°C, 70 hr, in Reference Fuel C |
ISO 175 | ||
邵氏 D,23℃,168 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 168 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,168 hr,在基准燃料中 Shore D, 23 ℃, 168 hr, in reference fuel |
ISO 175 | ||
邵氏 D,23℃,336 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 336 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,336 hr,在基准燃料C中 Shore D, 23 ℃, 336 hr, in reference fuel C |
ISO 175 | ||
邵氏 D,23℃,504 hr,在基准燃料A(异辛烷)中 Shore D, 23 ℃, 504 hr, in reference fuel A (isooctane) |
ISO 175 | ||
邵氏 D,23℃,504 hr,,在基准燃料C中 Shore D, 23 ℃, 504 hr, in reference fuel C |
ISO 175 | ||
邵氏 D,100℃,70 hr,在ASTM #1油中 Shore D, 100°C, 70 hr, in ASTM #1 Oil |
ISO 175 | ||
邵氏 D,100℃,70 hr,在ASTM #3油中 Shore D, 100 ℃, 70 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,168 hr,在ASTM #1油中 Shore D, 100°C, 168 hr, in ASTM #1 Oil |
ISO 175 | ||
邵氏 D,100℃,168 hr,在ASTM #3油中 Shore D, 100 ℃, 168 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,336 hr,在ASTM #1油中 Shore D, 100 ℃, 336 hr, in ASTM # 1 oil |
ISO 175 | ||
邵氏 D,100℃,336 hr,在ASTM #3油中 Shore D, 100 ℃, 336 hr, in ASTM # 3 oil |
ISO 175 | ||
邵氏 D,100℃,504 hr,在ASTM #1油中 Shore D, 100 ℃, 504 hr, in ASTM # 1 oil |
ISO 175 | ||
邵氏 D,100℃,504 hr,在ASTM #3油中 Shore D, 100 ℃, 504 hr, in ASTM # 3 oil |
ISO 175 | ||
体积变化 Volume change |
ASTM D471 | ||
23℃,70 hr,in Reference Fuel A 23℃,70 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ASTM D471 | |
23℃,168 hr,in Reference Fuel A 23℃,168 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel A 23℃,336 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel A 23℃,504 hr,in Reference Fuel A |
% | ASTM D471 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ASTM D471 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ASTM D471 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ASTM D471 | |
体积变化 Volume change |
ISO 175 | ||
23℃,70 hr,in Reference Fuel A 23℃,70 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,70 hr,甲醇 23 ℃, 70 hr, methanol |
% | ISO 175 | |
23℃,168 hr,in Reference Fuel A 23℃,168 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,168 hr,甲醇 23 ℃, 168 hr, methanol |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel A 23℃,336 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,336 hr,in Reference Fuel C 23℃,336 hr,in Reference Fuel C |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel A 23℃,504 hr,in Reference Fuel A |
% | ISO 175 | |
23℃,504 hr,in Reference Fuel C 23℃,504 hr,in Reference Fuel C |
% | ISO 175 | |
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ISO 175 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #1 Oil 100℃,168 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,168 hr,in ASTM #3 Oil 100℃,168 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #1 Oil 100℃,336 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,336 hr,in ASTM #3 Oil 100℃,336 hr,in ASTM #3 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #1 Oil 100℃,504 hr,in ASTM #1 Oil |
% | ISO 175 | |
100℃,504 hr,in ASTM #3 Oil 100℃,504 hr,in ASTM #3 Oil |
% | ISO 175 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
压缩载荷 Compression load |
ASTM D575 | ||
10% 挠曲 10% deflection |
MPa | ASTM D575 | |
15% 挠曲 15% deflection |
MPa | ASTM D575 | |
2% 挠曲 2% deflection |
MPa | ASTM D575 | |
20% 挠曲 20% deflection |
MPa | ASTM D575 | |
25% 挠曲 25% deflection |
MPa | ASTM D575 | |
5% 挠曲 5% deflection |
MPa | ASTM D575 | |
50% 挠曲 50% deflection |
MPa | ASTM D575 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 Post-cured 16 hr at 230°F |
4 速率 A (50°C/h) |
【新闻资讯】查看全部
欧洲PE和PP紧缺将因新增供应而有所缓解
2020-12-23 搜料网资讯: 2020年欧洲聚乙烯(PE)和聚丙烯(PP)市场并没有像许多人预期的那样结束,市场情绪在过去几周发生了显著变化。 2020年本来预计是一个糟糕的年份,因为主要来自美国的 |
欧洲PE和PP紧缺将因新增供应而有所缓解 搜料网资讯:2020年欧洲聚乙烯(PE)和聚丙烯(PP)市场并没有像许多人预期的那样结束,市场情绪在过去几周发生了显著变化。 2020年本来预计是一个糟糕的年份,因为主要来自美国的乙烷基PE的进口预计将以更大的供应量到达。 事实上,由于第一波新冠疫情让买家趋之若鹜,强烈的购买意愿使PE和PP包装需求增加。 其他行业则是停产,如PP使用量为10-11%的汽车行业。 到了下半年,大多数应用都恢复了正常。汽车业的表现好于预期,包装业也恢复到了正常水平。涉及到健康和卫生领域的行业,自始至终都保持良好。 家电行业在2020年下半年的复苏也超出预期,包括小型和大型家电。 年底聚烯烃购买量放缓已成常态,以前会有特殊的交易出现,以提高卖家的成交量,但2020年情况并非如此。 欧洲PE和PP的低价格意味着出口成为2020年第四季度的一大特点,导致市场紧张,尤其是PP行业。飓风劳拉阻止了美国的进口,这加剧了紧张的局面,为拉丁美洲和其他目的地创造了出口机会。 12月并不是一个充斥着廉价材料供应的淡季,PE和PP的价格都在上涨,特别是LDPE和PP。 乙烯合约与PE之间的价差从2019年的极低基数扩大到2020年。
价格在供应紧张的情况下上涨,而且一些生产商已经警告买家,这种上涨趋势很可能会持续到1月份。 在欧洲经济停滞数月后,欧洲最近的价格上涨正在缩小与亚洲价格的差距,而中国的相应价格则是由强劲的国内需求推动的,特别是自2020年第三季度中期以来的需求。 买家认为一些导致供应紧张的生产问题还能在12月和1月后恢复正常,从而缓解供应短缺。 然而,据许多消息来源称,进口预计要到第一季度才恢复,这将影响市场。 预计从2021年1月下旬起,新进口商品将抵达欧洲,中国国内需求将在农历新年假期前减速。据ICIS分析,这可能有助于调整各地区的价格。 每年的这个时候都在讨论2021年的年度合约,虽然目前的紧缺有利于卖方,但预计2021年下半年不会保持如此强劲的势头。 随着全球供应量的增加,预计PE将更容易获得。 在PE需求方面,ICIS分析预计,伴随着欧洲和全球经济状况改善的预期,2021年PE市场将缓慢但持续复苏。然而,2021年PE市场可能面临强劲的供应增加,因为预计2021年全球PE有效产能将比2020年增加6.5%。这可能会影响2021年的供需平衡。 特别是2021年全球HDPE的有效产能预计将同比增长8%以上,而同期全球LLDPE和LDPE产能预计将分别增长7%和3%。 2021年,PP供应量将大幅增加,尤其是在亚洲,届时将有770万吨/年的新产能投产,相当于2020年全球PP加工量的10%。对价格的影响预计将在下半年显现。 根据ICIS分析,在新冠疫情影响最严重的时期将结束的假设下,全球乙烯市场将在2021年出现好转迹象。经济增长和冠状病毒疫苗的分配及其效力的不确定性,可能会严重影响供需基本面。随着供应量的增加,欧洲乙烯有望保持势头。 从全球来看,到2021年,丙烯需求将以高于GDP的年均增长率增长,但这在很大程度上取决于全球经济的表现。 PP供应量也将增加,预计不会出现供应紧张的情况,也不会出现与PE相同的供过于求的局面。 最终,亚洲——尤其是中国的需求,将对2021年欧洲的PE和PP的走势产生重大影响。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
加工方式 | |||
---|---|---|---|
注射 | Nominal Value | Unit | |
干燥温度 - 热风干燥机 | °C | ||
干燥时间 - 热风干燥机 | hr | ||
建议的最大水分含量 | % | ||
建议注射量 | % | ||
建议的最大回制料比例 | % | ||
料筒后部温度 | °C | ||
料筒中部温度 | °C | ||
料筒前部温度 | °C | ||
射嘴温度 | °C | ||
加工(熔体)温度 | °C | ||
模具温度 | °C | ||
注塑压力 | MPa | ||
注射速度 | |||
背压 | MPa | ||
螺杆转速 | rpm | ||
锁模力 | kN/cm² | ||
垫层 | mm | ||
螺杆长径比 | |||
螺杆压缩比 | |||
挤出 | Nominal Value | Unit | |
干燥温度 | °C | ||
干燥时间 | hr | ||
料筒1区温度 | °C | ||
料筒2区温度 | °C | ||
料筒3区温度 | °C | ||
接头温度 | °C | ||
熔体温度 | °C | ||
口模温度 | °C |