牌号简介 About |
---|
HD53TA010是一种高密度聚乙烯(HDPE)级产品,专门用于生产防水油布、包装织物等拉伸带制品和其他具有良好韧性和延伸性的挤压制品。它具有很好的加工性、低的水携带性和拉伸性、较低的电机负载和较高的输出功率,再加上良好的胶带性能,使其成为一个等级的选择。这种材料特别适合制作低旦带。 HD53TA010 is a High Density Polyethylene (HDPE) grade produced and specially formulated to manufacture stretched tape products such as Tarpaulins and Wrapping fabrics and other extrusion products with good combination of tenacity and elongation. It has very good processability, low water carry - over and stretchability, less motor load and high output combined with good tape properties to make it a grade of choice. This material is particularly suitable for making low denier tapes |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.955 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.2 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,注塑成型 Yield, injection molding |
22.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
屈服,注塑成型 Yield, injection molding |
15 | % | ASTM D638 |
弯曲模量 Bending modulus |
|||
注塑成型 injection molding |
800 | MPa | ASTM D790 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
注塑 Injection molding |
ASTM D256 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
「原油收盘」非农“爆冷”暗示经济复苏不稳 两大原油期货再度转跌
2021-09-06 搜料网资讯: 在艾达(Ida)热带风暴导致美国墨西哥湾减产后,市场担心美国石油供应仍将有限,这限制了减产幅度。美国公布的就业报告逊于预期,显示经济复苏不稳,这可能意味着在 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |