牌号简介 About |
---|
Elix Ultra HH 4115 Hi超高耐热abs,具有极强的抗冲击性ISO shortname:ISO 2580-1 abs 2-x,mg,115-15-35-20优点:具有极强的抗冲击性,低温延展性,极高的抗冲击性,高达-30°C,流动性和耐热性良好,比PC/abs低密度,低排放和气味等级,低模具沉积。其在注塑加工中的应用较好的尺寸热下化学成分:聚碳酸酯改性的丙烯腈-丁二烯-苯乙烯共聚物(ABS)和聚(苯乙烯-马来酰亚胺) ELIX ULTRA HH 4115 HI Very high heat resistance ABS with extreme impact resistance ISO shortname: ISO 2580-1 ABS 2-X, MG, 115-15-35-20 Major Benefits: Extreme impact resistance with low temperature ductility Very high impact up to -30°C Well balanced flowability and heat resistance Lower density than PC/ABS Low emission and odor grade Lower mould deposits in injection molding processing applications Better dimensional under heat Chemical Composition: Acrylonitrile-butadiene-styrene (ABS) copolymer modified with polycarbonate and poly(styrene-co-maleimide) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
25℃ 25℃ |
1.07 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,5 kg 260℃,5 kg |
14.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate 2 |
ISO 2577 | ||
TD TD |
0.65 to 0.75 | % | ISO 2577 |
MD MD |
0.65 to 0.75 | % | ISO 2577 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
40 | kJ/m² | ISO 179/1eA |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
燃烧速率 Burning rate 4 |
|||
2.0 mm 2.0 mm 4 |
mm/min | ISO 3795 | |
碳排放 carbon emission |
|||
Total,23℃ Total,23℃ |
µgC/g | VDA 277 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
排放 discharge |
VDA 278 | ||
FOG total:23℃ FOG total:23℃ |
µg/g | VDA 278 | |
VOC total:23℃ VOC total:23℃ |
µg/g | VDA 278 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/50 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 3 |
|||
23℃ 23℃ 3 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
|||
23℃ 23℃ |
MPa | ISO 178 | |
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2 mm |
3 0.079 in/min |
4 US - FMVSS |
【新闻资讯】查看全部
塑料薄膜见得多 你真了解它吗?
2017-09-28 塑料薄膜是指用聚氯乙烯、聚乙烯、聚丙烯、聚苯乙烯以及其他树脂为主要原料,并于其它助剂按一定的比例均匀混合后,在塑料成型机械设备上成型为有一定厚度(厚度为0.01-0.25mm)、宽度和无限长度的、表面平整、光滑而柔软的塑料制品。 一、塑料薄膜的用途 塑料薄膜 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |