MVR(300°C/1.2 kg)6.0 cm³/10分钟;通用;高粘度;紫外线稳定;易释放;注塑-熔融温度280-320°C;可提供透明、半透明和不透明三种颜色选择。 MVR (300°C/1.2 kg) 6.0 cm³/10 min; general purpose; high viscosity; UV stabilized; easy release; injection molding - melt temperature 280 - 320°C; available in transparent, translucent and opaque colors |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.66 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
6.5 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
6.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD TD |
0.60 to 0.80 | % | ISO 2577 |
MD MD |
% | ISO 2577 | |
TD:2.0 mm TD:2.0 mm |
% | ISO 294-4 | |
MD:2.0 mm MD:2.0 mm |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
水气透过率 Water vapor transmittance |
|||
23℃,85% RH,100 µm 23℃,85% RH,100 µm |
g/m²/24 hr | ISO 15106-1 | |
气体渗透 Gas permeation |
ISO 2556 | ||
二氧化碳:23℃,25.4 µm Carbon dioxide: 23 ℃, 25.4 µ m |
cm³/m²/bar/24 hr | ISO 2556 | |
二氧化碳:23℃,100.0 µm Carbon dioxide: 23 ℃, 100.0 µ m |
cm³/m²/bar/24 hr | ISO 2556 | |
氮气:23℃,25.4 µm Nitrogen: 23 ℃, 25.4 µ m |
cm³/m²/bar/24 hr | ISO 2556 | |
氮气:23℃,100.0 µm Nitrogen: 23 ℃, 100.0 µ m |
cm³/m²/bar/24 hr | ISO 2556 | |
氧气:23℃,25.4 µm Oxygen: 23 ℃, 25.4 µ m |
cm³/m²/bar/24 hr | ISO 2556 | |
氧气:23℃,100.0 µm Oxygen: 23 ℃, 100.0 µ m |
cm³/m²/bar/24 hr | ISO 2556 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 7391 | ||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 7391 | |
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ISO 7391 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-60℃ -60℃ |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/A | ||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 180-A | |
23℃,局部断裂 23 ℃, localized fracture |
kJ/m² | ISO 180-A | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
-30℃ -30℃ |
J | ISO 6603-2 | |
23℃ 23℃ |
J | ISO 6603-2 | |
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
ISO 6603-2 | ||
-30℃ -30℃ |
N | ISO 6603-2 | |
23℃ 23℃ |
N | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
玻璃化转变温度 Glass transition temperature |
℃ | ISO 11357-2 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
137℃ 137℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
|||
23℃ 23℃ |
W/m/K | ISO 8302 | |
相对温度指数 Relative temperature index |
|||
电气性能,1.50 mm Electrical performance, 1.50 mm |
℃ | UL 746 | |
强度机械性能,1.50 mm Strength mechanical performance, 1.50 mm |
℃ | UL 746 | |
冲击机械性能,1.50 mm Impact mechanical performance, 1.50 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
解决方案 A Solution A |
V | IEC 60112 | |
解决方案 B Solution B |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
小型燃烧器火焰的应用 The Application of Small Burner Flames |
|||
Method K and F,2.00 mm Method K and F,2.00 mm |
DIN 53438-1, -3 | ||
燃烧速率 Burning rate |
|||
USFMVSS,> 1.00 mm USFMVSS,> 1.00 mm |
ISO 3795 | ||
Flash Ignition Temperature Flash Ignition Temperature |
℃ | ASTM D1929 | |
Glow Wire Test Glow Wire Test |
EDF HN60 E.02 | ||
1.50 mm 1.50 mm |
℃ | EDF HN60 E.02 | |
3.00 mm 3.00 mm |
℃ | EDF HN60 E.02 | |
针焰测试 Needle flame test |
IEC 60695-11-5 | ||
Method F:1.50 mm Method F:1.50 mm |
min | IEC 60695-11-5 | |
Method F:2.00 mm Method F:2.00 mm |
min | IEC 60695-11-5 | |
Method F:3.00 mm Method F:3.00 mm |
min | IEC 60695-11-5 | |
Method K:2.00 mm Method K:2.00 mm |
min | IEC 60695-11-5 | |
Method K:3.00 mm Method K:3.00 mm |
min | IEC 60695-11-5 | |
自燃温度 Autoignition temperature |
℃ | ASTM D1929 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ISO 489 | ||
透光率 Transmittance |
ISO 13468-2 | ||
1000 µm 1000 µm |
% | ISO 13468-2 | |
2000 µm 2000 µm |
% | ISO 13468-2 | |
3000 µm 3000 µm |
% | ISO 13468-2 | |
4000 µm 4000 µm |
% | ISO 13468-2 | |
雾度 Haze |
|||
3000 µm 3000 µm |
% | ISO 14782 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
|||
23℃ 23℃ |
IEC 60426 | ||
ISO Shortname ISO Shortname |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/50 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/50 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2/50 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
ISO 178 | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Bending strain |
% | ISO 178 | |
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Pellets |
3 60x60x2 mm, 500 bar |
4 0.079 in/min |
5 2 mm/min |
6 Based on ISO 179-1eA, 3 mm |
7 3.2 mm |
8 10°C/min |
9 Cross-flow |
10 程序 A |
11 方法 A |
【新闻资讯】查看全部
什么是PVC吸塑工艺?
2017-10-13 pvc吸塑是一种塑料加工工艺,主要的原理是将平展的pvc塑料片材加热,然后变软后,采用真空吸附于模具的表面,在经过冷却之后成型,进而可以广泛的应用于塑料的包装,灯饰.广告.装饰等相关的行业. 吸塑包装制品主要包括:泡壳.托盘.吸塑盒.也被称为:真空罩.泡罩等,吸塑包装的设备主要包括:吸塑成型机.冲床.封口机.高频机.折变机等,封装形成的包装产品也可以分为:插件.吸卡双泡壳. |
什么是PVC吸塑工艺? pvc吸塑是一种塑料制作工艺,关键的基本原理是将平整的pvc塑料塑胶板材加温,随后变松后,选用真空泵吸咐于模貝的表面,在历经制冷以后成形,从而能够 普遍的运用于塑料的包裝,照明灯饰.广告宣传.装饰设计等有关的领域. 吸塑塑料包装制品关键包含:泡壳.拖盘.吸塑盒.也被称作:真空泵罩.泡罩等,吸塑包裝的机器设备关键包含:吸塑成形机.高速冲床.全自动封口机.高频加热机.折变机等,封装产生的包裝商品还可以分成:软件.吸卡双泡壳.半泡壳.折起来泡壳.三折泡壳等. 在选用吸塑加工工艺将全透明的塑料片材制成特殊的突起形的全透明塑料,罩于商品表面,具有维护及其清理商品的功效,将一般的塑料硬,在表面上沾到一层物质的量浓度的原材料,进而使拖盘表面有一种物质的量浓度的触感,以用于提升包装用品的级别, 选用独特加工工艺改性工程塑料的吸塑拖盘,该原材料表面的阻值低于10的11次放欧母.关键用以电子器件.IT商品的静电感应拖盘. 吸塑生产制造用的模貝,成本费最少是的熟石膏模,次之的是电镀铜模,较贵的是铝合金模板,模貝钻好小圆孔,用以真空泵吸咐热化的片材,产生吸塑商品. 大家常讲的吸塑,选用吸塑成形机将热变软的塑料片材吸咐于模貝表面,制冷后,产生凸凹样子的塑料. 吸塑裁剪:吸塑包裝成形后的塑料商品,历经高速冲床,将盛德美的塑胶板材用激光刀模分为单独的商品. 压边:pvc吸塑包装用品中有一种叫软件包裝,必须将泡壳的三个边用折机折到身后,便于在下道封装工艺流程中,将卡纸插进折边内,产生装卡包裝. 热熔密封:是一种吸塑封装加工工艺,用全自动封口机将表面涂有吸塑油的卡纸与泡壳也和在一起,产生吸卡包裝, 高频率密封:便是一种吸塑封装的加工工艺,主要是用高周波机造成超音波,随后将泡壳与泡壳黏合于一起,产生双泡壳的包裝,与高频率密封所不一样的是,超音波不仅能够 封PVC.PET.PETG等原材料,还可以封PET的原材料,并且针对封装的商品沒有有磁感应的损害,尤其合适电子设备的封装:但是缺陷是取决于超音波包边只有间距的斑点状,并且一般得话,每一次只有封一条边. 来源于:互联网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。