牌号简介 About |
---|
CALIBRE™ 302V-6 LD HC18010009聚碳酸酯是一种乳白色挤压级树脂,含有专利的光扩散包,为电子标牌和照明应用提供了良好的光传输、光扩散和白度组合,并专门设计用于LED光源。CALIBRE™ 302V-6 LD HC18010009是紫外线稳定,具有优异的抗冲击性,热变形性,并符合UL94V-2额定值。应用:LED背光标志面和频道字母符合:CSA(加拿大标准协会)UL(美国保险商实验室公司) CALIBRE™ 302V-6 LD HC18010009 Polycarbonate is an opalescent white extrusion-grade resin containing a proprietary light diffusion package that offers an excellent combination of light transmission, light diffusion and whiteness for electronic signage and lighting applications and has been specifically designed to be used with LED light sources. CALIBRE™ 302V-6 LD HC18010009 is UV stabilized, has outstanding impact resistance, heat distortion resistance, and meets UL94 V-2 rating. Applications: LED back-lit sign faces and channel letters Complies with: CSA (Canadian Standards Association) UL (Underwriters Laboratory, Inc.) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
6.0 | g/10min | ASTM D1238 |
300℃,1.20kg 300℃,1.20kg |
5.6 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 to 0.70 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ASTM D570 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
23℃,24hr 23℃,24hr |
% | ASTM D570 | |
23℃,24hr 23℃,24hr |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength 2 |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
屈服 yield 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 4 , 5 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 , 5 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 180-A | |
23℃ 23℃ |
ASTM D256 | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ISO 180 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 6 |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance 7 |
ASTM D1003 | ||
3200 µm 3200 µm |
% | ASTM D1003 | |
4500 µm 4500 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 方法 I (三点负荷), 0.079 in/min |
4 0.079 in/min |
5 3 点 |
6 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
7 为 3.2 mm(0.125 英寸)和 4.5 mm(0.177 英寸)厚度的共挤片材确定的透光值,包含 XZ 94219.04 聚碳酸酯树脂的一个 0.125 mm(0.005 英寸)厚度的 UV 保护盖层。 |
【新闻资讯】查看全部
加拿大蒙特利尔拟禁塑料瓶 遭饮品协会三大企业抵抗
2016-03-22 据英国《独立报》3月19日报道,加拿大蒙特利尔市市长丹尼斯・科德尔表示有意出台一项法令,禁止全市人民和企业使用塑料瓶。该法令目前遭到了以可口可乐、百事可乐、雀巢为首等企业的反对。 据悉,丹尼斯・科德尔早前曾宣布将禁止使用塑料袋。而限制使用塑料袋的禁令将于2018年开始逐步实行。 报道称,加拿大饮品协会代表包括以可口可乐、百事可乐和雀巢三大企业在内的60多家企业,该协会于3月份向说客登记处提交了一份文件。文件上写道:“使用塑料瓶对顾客来说,既安全又便利,禁止使 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |