牌号简介 About |
---|
用途:玻璃纤维层间光学膜、织物层间粘合膜、粗化特性:哑光透明、不发黄、低软化点夹层 Applications: Optical interlayer film for glass lamination Adhesive interlayer for textile lamination, armoring Characteristics: Matte finish Clear, non-yellowing Low softening point Interleaf |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate 2 |
5.0 | g/10min | ASTM D1238 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
极限 limit |
41.4 | MPa | ASTM D412 |
100% 应变 100% strain |
3.31 | MPa | ASTM D412 |
200% 应变 200% strain |
MPa | ASTM D412 | |
300% 应变 300% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture 3 |
% | ASTM D412 | |
撕裂强度 tear strength |
|||
1.27 mm 1.27 mm |
kN/m | ASTM D1004 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
|||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
黄度指数 Yellowness index |
YI | ASTM D1925 | |
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
77 | ASTM D2240 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 175°C |
3 Ultimate |
【新闻资讯】查看全部
倍耐力轮胎采用银胶菊做橡胶资料
2015-12-25 近日,倍耐力首次使用源自植物银胶菊的天然橡胶生产超高性能轮胎,并在维佐拉和巴洛科测试赛道使用玛莎拉蒂Ghibli成功试跑。这种非粮食作物在干旱气候中非常典型,可以在无农药和少水的条件下培育,因而可以成为橡胶树的替代品。 这款创新的概念胎创记录地只用了两年时间,就从最初的原材料研究到了实体赛道试跑。2013年时,倍耐力与意大利石化巨头Eni集团旗下化工企业Versalis公司签订协议,由对方独家供应银胶菊天然橡胶,用于轮胎生产。在极短的周期内,倍耐力的研发人员在实验室环境下深 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |